综合评述了碱激发胶凝材料及其混凝土的研究进展,总结了影响碱激发胶凝材料性能的主要因素,着重介绍了采用碱激发胶凝材料配制的混凝土性能最新研究进展,包括新拌混凝土拌合物和易性、硬化混凝土强度和抗化学侵蚀、碱集料反应、对钢筋的保护作用等耐久性问题以及硬化混凝土变形性能等,并提出当前研究存在的问题和今后研究的发展方向。
Abstract：Research on alkali-activated binders and concrete made with alkali-activated binders are reviewed.Factors affecting the properties of the alkali-activated cement are summarized and emphasis is placed on the properties of concrete made with al- kali-activated binders,including the workability of the fresh concrete,the strength,deformation and durability such as chemical attack resistance,alkali-aggregate reaction and protection of the steel bar in reinforced concrete.Some suggestions for future investigations are also made.
[1]PURDON A O.The action of alkali on blast furnace slag [J].J Soc Chem Ind,1940,59:191-202.
[2]杨南如．碱胶凝材料形成的物理化学基础(1)[J]．硅酸盐学报，1996，24(2)：209-215．YANG Nanru.J Chin Ceram Soc (in Chinese),1996,24(2):209-215.
[3]ROY D M.Alkali-activated cements:opportunities and challenges [J]. Corn Concr Res,1999,29:249-254.
[4]杨长辉，蒲心诚．论碱矿渣水泥及混凝土的缓凝问题及缓凝方法[J]．重庆建筑大学学报，1996，18(3)：67-72．YANG Changhni,PU Xincheng.J Chongqing Jianzhu Univ (in Chi- nese),1996,18(3):67-72.
[5]ROY D M,SILSBEE M R,WOLFE-CONFER D.New rapid setting alkali activated cement compositions [J].MRS Proc,1990,179:203- 220.
[6]DOUGLAS E.,BILODEAU A,MALHOTRA V M.Properties and durability of alkali-activated slag concrete [J].ACI Mater J,1992, 89(5):509-516.
[7]COLLINS F,SANJAYAN J G Strength and shrinkage properties of alkali-activated slag concrete containing porous coarse aggregate [J]. Cem Concr Res,1999,29:607-610.
[8]BAKHAREV T,SANJAYAN J G,Cheng Y B.Alkali activation of Australian slag cements [J].Cem Concr Res 1999,29:113-120.
[9]COLLINS F,SANJAYAN J G.Workability and mechanical properties of alkaliactivated slag concrete [J].Cem Concr Res,1999,29:455- 458.
[10]DAVIDOVITS J.Geopolymers:inorganic polymeric new materials [J]. J Therm Anal,1991,37 (8):1633-1656.
[11]张书政，龚克成．地聚合物[J]．材料科学与工程学报，2003，21(3)：430-436．ZHANG Shuzheng,GONG Kecheng.J Mater Sci Eng (in Chinese), 2003,21(3):430-436.
[12]DUXSON P,FERN■NDEZ-JIM■NEZ A,PROVIS J L,et al.Geo- polymer technology:the current state of the art [J].J Mater Sci,2007, 42(9):2917-2933.
[13]王晴，刘磊，吴昌鹏，等．矿渣基无机矿物聚合材料力学性能的研究[J]．沈阳建筑大学学报，2007，23(1)：73-76．WANG Qin,LIU Lei,WU Changpang,et al.J Shenyang Jianzhu Univ (in Chinese),2007,23(1):73-76.
[14]武俊宇，曾荣树，倪文，等．高钙粉煤灰在建材行业的研究进展[J]．硅酸盐通报，2007，26(4)：753-759．WU Junyu,ZENG Rongshu,NI Wen,et al.Bull J Chin Ceram Soc (in Chinese),2007,26(4):753-759.
[15]DAVIDOVITS J.Method for obtaining a geopolymeric binder allow- ing to stabilize,solidify and consolidate toxic or waste materials [P]. US patent,5539140,1996-07-23.
[16]WANG S D,SCRIVENER K L.Hydration products of alkali activated slag cement [J].Cem Concr Res,1995,25(3):561-571
[17]SHI C,XIE P.Interface between paste and quartz sand in alkali-slag mortars [J].Cem Concr Res,1998,28:887-896.
[18]陈友治，蒲心诚，马保国，等．Na_2SO_4-矿渣水泥的水化与硬化特性研究[J]．硅酸盐学报，2000，28(增刊)：81-84．CHEN Youzhi,PU Xincheng,MA Baoguo,et al.J Chin Ceram Soc (in Chinese),2000,28(suppl):81-84.
[19]徐彬，蒲心诚．固态碱组分碱矿渣水泥水化产物研究[J]．西南工学院学报，1997(3)：29-34．XU Bin,PU Xincheng.J Xinan Univ Technol (in Chinese),1997(3): 29-34.
[20]ALONSO S,PALOMO A.Calorimetric study of alkaline activation of calcium hydroxide-metakaolin solid mixes [J].Cem Concr Res,2001, 31:25-30.
[21]YIP C K,LUKEY G C,van DEVENTER J S J.The coexistence of geopolymeric gel and calcium silicate hydrate at the early stage of al- kaline activation [J].Cem Concr Res,2005,35(9):1688-1697.
[22]PALOMO A,GRUTZECK M W,BLANCO M T.Alkali-activated fly ashes:A cement for the future [J].Cem Concr Res,1999,29:1323- 1329.
[23]JAARSVELD J G S,van DEVENTER J S J,LUKEY G C.The char- acterization of source materials in fly ash-based geopolymers [J].Ma- ter Lett,2003,57(7):1272-1280.
[24]HARDJITO D,WALLAH S E,SUMAJOUW D M J,et al.On the development of fly ash-based geopolymer concrete [J].ACI Mater J, 2004,101(6):467-472.
[25]PALOMO A,ALONSO S,FERNANDEZ-JIMENEZ A.Alkaline activation of fly ashes.A NMR study of the reaction products [J].J Am Ceram Soc,2004,87(6):1141-1145.
[26]BAKHAREV T.Geopolymeric materials prepared using Class F fly ash and elevated temperature curing [J].Cem Concr Res,2005,35: 1224-1232.
[27]PUERTAS F,MART■NEZ-RAM■REZ S,ALONSO S,et al. Alkali-activated fly ash/slag cement,strength behaviour and hydration products [J].Cem Concr Res,2000,30:1625-1632
[28]DOMBROWSKI K,BUCHWALD A,WEIL M.The influence of calcium content on the structure and thermal performance of fly ash based geopolymers [J].J Mater Sci,2007,42(9):3033-3043.
[29]LI Zongjin,LIU Sifeng.Influence of slag as additive on compressive strength of fly ash-based geopolymer [J].J Mater Civil Eng,2007, 19(6):470-474.
[30]BUCHWALD A,DOMBROWSKI K,WEIL M.The influence of calcium content on the performance of geopolymeric binder especially the resistance against acids [A]//4th International Conference on Geo- polymers [C],St Quentin,France.
[31]AWI■ C D,BILIM C,■ELIK ■,et al.Influence of activator on the strength and drying shrinkage of alkali-activated slag mortar [J].Con- stru Building Mater,doi:10.1016/j.conbuildmat.2007-10-11.
[32]XU Hua,DEVENTER J S J.The geopolymerisation of alumi-silicate minerals [J].Inter J Mineral Proc,2000,59(3):247-266.
[33]PANAGIOTOPOULOU Ch,KONTORI E,PERRAKI Th,et al.Dis- solution of alumisilicate minerals and by-products in alkaline media [J]. J Mater Sci,2007,42:2967-2973.
[34]芦令超，沈晓冬，严生，等．细度对碱矿渣水泥强度和水化程度的影响[J]．水泥·石灰，1995(2)：15-18 LU Lingchao,SHEN Xiaodong,YAN Sheng,et al.Cem Lime (in Chinese),1995(2):15-18.
[35]WANG S D,SCRIVENER K L,PRATT P L.Factors affecting the strength of alkali-activated slag [J].Cem Concr Res,1994,24(6): 1033-1043.
[36]KUMAR R,Kumar S,MEHROTRA S P.Towards sustainable solu- tions for fly ash through mechanical activation [J].Resources,Conserv Recycling,2007,52:157-179.
[37]翁履谦，SAGOE-CRENTSIL K，宋申华，等．地质聚合物合成中铝酸盐组分的作用机制[J]．硅酸盐学报，2005，33(3)：276-280．WENG Lüqian,SAGOE-CRENTSIL K,SONG Shenhua,et al.J Chin Cerem Soc (in Chinese),2005,33(3):276-280.
[38]DAVIDOVITS J.Chemistry of geopolymeric systems:Terminology [A]//Proceedings of 99 Geopolymer Conference [C],1999,1:9-40.
[39]BARBOSA V F,MACKENZIE K J,THAUMATURGO C.Synthesis and characterization of materials based on inorganic polymers of alu- mina and silica:sodium polysialate polymers [J].Int J Inorg Polym 2000,2:309-317.
[40]DUXSON P,PROVIS J L,LUKEY G C,et al.Understanding the relationship between geopolymer composition,microstructure and mechanical properties [J].Colloids Surf A,2005,269:47-58.
[41]FLETCHER R A,MACKENZIE K J D,NICHOLSON C L,et al.The composition range of alumino silicate geopolymers [J].J Eur Ceram Soc,2005,25:1471-1477.
[42]FERNANDEZ-JIMENEZ A,PALOMO J,SOBRADOS I,et al.The role played by reactive alumina content in the alkaline activation of fly ashes [J].Micropor Mesopor Mater,2006,91:111-119.
[43]SUN Peijiang.Fly ash based irganic polymeric building material [D]. Wayne State University,Detroit,Michigan,2005.
[44]YIP C K,LUKEY G C,PROVIS J L,et al.Effect of calcium silicate sources on geopolymerisation [J].Cem Concr Res,2008,38:554-564.
[45]SHI C.Strength,pore structure and permeability of alkali-activated slag mortars [J].Cem Concr Res,1996,26:1789-1800.
[46]LEE W K W,van DEVENTER J S J.The effects of irganic salt con- tamination on the strength and durability of geopolymers [J].Colloids Surf A,2002,211:115-126.
[47]KOVALCHUK G,FERNANDEZ-JIMENEZ A,PALOMO A,Alkali- activated fly ash:Effect of thermal curing conditions on mechanical and microstructural development-PartⅡ[J].Fuel,2007,86:315-322.
[48]TEIXEIRA-PINTO A,FERNANDES P,JALALI S.Geopolymer Manufacture and Application-Main problems When Using Concrete Technology [A]//Geopolymers 2002 International Conference [C], Melbourne,Australia,Siloxo Pry Ltd.,2002.
[49]BAKHAREV T,SANJAYAN J G,CHENG Y B.Effect of admixtures on properties of alkali-activated slag concrete [J].Cem Concr Res, 2000,30(9):1367-1374.
[50]PUERTAS F,PALOMO A,FERNANDEZ-JIMENEZ A,et al.Effect of superplasticisers on the behaviour and properties of alkaline cements [J].Adv Cem Res,2003,15(1):23-28.
[51]PALACIOS M,PUERTAS F.Effect of superplasticizer and shrink- age-reducing admixtures on alkali-activated slag pastes and mortars [J]. Cem Concr Res,2005,35:1358-1367.
[52]PALACIOS M,PUERTAS F.Stability of superplasticizer and shri- kagereducing admixtures in high basic media [J].Mater Construe, 2004,54(276):65-86.
[53]WALLAH S E,RANGAN B V.Low-calcium fly ash-based geo- polymer concrete:long-term properties [R].Research Report GC 2, Faculty of Engineering,Curtin University of Techlogy,Perth,Australia, 2006.
[54]CHINDAPRASIRT P,CHAREERAT T,SIRIVIVATNAN V.Workabil- ity and strength of coarse high calcium fly ash geopolymer [J].Cem Concr Comp,2007,29:224-229.
[55]ANDINI S,CIOFFI R,COLANGELO F,et al.Coal fly ash as raw material for the manufacture of geopolymer-based products [J].Waste Management,2008,28(2):416-423.
[56]ACHECO-TORGAL P F,CASTRO-GOMES J,JALALI S.Investiga- tions about the effect of aggregates on strength and microstructure of geo-polymeric mine waste mud binders [J].Cem Concr Res,2007,37: 933-941.
[57]张云升，孙伟，林玮，等．用环境扫描电镜原位定量追踪K-PSDS型地聚合物混凝土界面区的水化过程[J]．硅酸盐学报，2003，31(8)：806-810．ZHANG Yunsheng,SUN Wei,LIN Wei,et al.J Chin Ceram Soc (in Chinese),2003,31(8):806-810.
[58]LEE W K W,DEVENTER J S J.Chemical interactions between siliceous aggregates and low-Ca alkali-activated cements [J].Cem Concr Res,2007,37:844-855.
[59]PALOMO M T,BLANCO-VARELA M L,GRANIZO F,et al.Chemi- cal stability of cementitious materials based on metakaolin [J].Cem Concr Res,1999,29:997-1004.
[60]FERNANDEZ-JIMENEZ A,GARCIA-LODEIRO I,PALOMO A. Durability of alkali-activated fly ash cementitions materials[J].J Ma- ter Sci,2007,42:3055-3065.
[61]BAKHAREV T.Resistance of geopolymer materials to acid attack[J]. Cem Concr Res,2005,35:658-670.
[62]BAKHAREV T.Durability of geopolymer materials in sodium and magnesium sulfate solutions[J].Cem Concr Res,2005,35:1233- 1246.
[63]BAKHAREV T,SANJAYANA J G,CHENG Y B.Sulfate attack on alkali-activated slag concrete[J].Cem Concr Res,2002,32:211-216.
[64]BAKHAREV T,SANJAYANA J G,CHENG Y B.Resistance of alkali-activated slag concrete to acid attack[J].Cem Concr Res,2003, 33:1607-1611.
[65]周焕海，唐明述，吴学权，等．碱矿渣水泥浆体的孔结构和强度[J]．硅酸盐通报，1994，13(3)：15-19．
[66]ZHOU Huanhai,TANG Mingshu,WU Xuequan,et al.Bull J Chin Ceram Soc(in Chinese),1994,13(3):15-19.
[66]CHEN W,BROUWERS H J H.The hydration of slag,part 1:reaction models for alkali-activated slag[J].J Mater Sci,2007,42:428-443.
[67]LI,Keliang;HUANG Guohong,JIANG,Linhua,et al.Study on abili- ties of mineral admixtures and Geopolymer to restrain ASR[J].Key Eng Mater,2006,302-303:248-254.
[68]GIFFORD P M,GILLOTT J E.Alkali-silica reaction(ASR)and alkali-carbonate reaction(ACR)in activated blast furnace slag cement (ABFSC)concrete[J].Cem Concr Res,1996,26(1):21-26.
[69]杨长辉，蒲心诚，吴芳．碱矿渣水泥砂浆的碱集料反应膨胀研究[J]．硅酸盐学报，1999，27(6)：651-657．
[70]YANG Changhui,PU Xincheng,WU Fang.J Chin Ceram Soc(in Chinese),1999,27(6):651-657.
[70]BAKHAREV T,SANJAYANA J G,CHENG Y B.Resistance of alkali-activated slag concrete to alkali-aggregate reaction[J].Cem Concr Res,2001,31:331-334.
[71]FERNANDEZ-JIMENEZ A,PUERTAS F.The alkali-silica reaction in alkali-activated granulated slag mortars with reactive aggregate[J]. Cem Concr Res,2002,32:1019-1024.
[72]GARCIA-LODEIRO I,PALOMO A,FERNANDEZ-JIMENEZ A. Alkali-aggregate reaction in activated fly ash systems[J].Cem Concr Res,2007,37:175-183.
[73]YODMUNEE S,YODSUDJAI W.Study on corrosion of steel bar in fly ash-based geopolymer concrete,International Conference on Poz- zolan,Concrete and Geopolymer,Khon Kaen,Thailand,2006:72-80.
[74]MIRANDA J M,FERNANDEZ-JIMENEZ A,GONZALEZ J A,et al. Corrosion resistance in activated fly ash mortars[J].Cem Concr Res, 2005,35:1210-1217.
[75]SHI Caijun.Strength,pore structure and permeability of alkali-acti- vated slag mortars[J].Cem Concr Res,1996,26(12):1789-1799.
76张云升，孙伟，沙建芳，等．粉煤灰地聚合物混凝土的制备特性及机理[J]．建筑材料学报，2003，6(3)：237-242．ZHANG Yunsheng,SUN Wei,SHA Jianfang,et al.J Building Ma- ter(in Chinese),2003,6(3):237-242.
77]李克亮，蒋林华，黄国泓，等．地聚合物复合水泥混凝土性能研究[J]．水利水运工程学报，2006(1)：49-53．LI Keliang,JIANG Linhua,HUANG Guohong,et al.J Hydro-Sci Eng (in Chinese),2006(1):49-53.
[78]BAKHAREVA T,SANJAYANA J G,CHENG Y B.Resistance of alkali-activated slag concrete to carbonation[J].Cem Concr Res,2001, 31:1277-1283.
[79]AL-OTAIBI S.Durability of concrete incorporating GGBS activated by water-glass[J].Constr Build Mater,2008,22:2059-2067.
[80]DEJA J.Carbonation aspects of alkali activated slag mortars and concretes[J].Sil Ind,2002,67(3-4):37-42.
[81]BYFORS K.in Proc.3rd Int.Conf.on Fly Ash,Silica Fume,Slag and Natural Pozzolans in Concrete.Trondheim,SP114-70,1989,2:1547.
[82]XU H,PROVIS J L,van DEVENTER J S J,et al.Characterization of aged slag concretes[J].ACI Mater J,2008,105(2):131-139.
83廖佳庆．碱矿渣水泥与混凝土化学收缩和干缩行为研究D．重庆：重庆大学学位论文，2007．LIAO Jiaqing.Chemical and drying shrinkage of the alkali-activated slag cement and concrete(in Chinese,dissertation).Chongqing:Chong- qing University,2007.
[84]ANTONIO A,MELO N,MARIA A C,et al.Drying and autogenous shrinkage of pastes and mortars with activated slag cement[J].Cem Conct Res,2008,38:565-574.
[85]SOFI M,DEVENTER J S J,MENDIS P A,et al.Engineering proper- ties of inorganic polymer concretes[J].Cem Concr Res,2007,37: 251-257.
基本信息:
中图分类号:TU528
引用信息:
[1]孔德玉,张俊芝,倪彤元,等.碱激发胶凝材料及混凝土研究进展[J].硅酸盐学报,2009,37(01):151-159.
基金信息:
浙江省科技计划项目(2007C23058);; 杭州市科技计划项目(20070733B20)。