研究珍珠岩基新型复合保温材料是开拓矿物材料应用领域的新课题。本工作研究了2种不同尺寸珍珠岩以及气相二氧化硅作为复合填料，分别以捏合工艺和直接混合工艺填充于乙烯基硅油或室温硫化硅橡胶，制备珍珠岩填充的复合硅橡胶保温板，通过检测不同产物的导热系数以及保温效果来评价其性能。结果表明：以捏合工艺制备的产品会降低珍珠岩的保温效果，主要原因是中空颗粒被捏合过程破碎；而以气相二氧化硅为主要填料制备的保温板不易成型，可成型产品最低导热系数为0.172 8 W·m?1·K?1；当以珍珠岩+气硅粉在硅橡胶中的质量比为37.5%时，产品导热系数为0.034 9 W·m?1·K?1，产物厚度为2.5 cm、250℃单侧加热4 min后，背面温度为67℃，基本满足在新型烟具等特种保温隔热应用要求。
Abstract：Developing some thermal insulating composite materials based on perlite is a subject to expand the application of mineral materials.In this paper,the vinyl silicone oil or room-temperature vulcanized silicone rubber was mixed with two kinds of perlite with different sizes and fumed silica as fillers through a kneading process and a direct mixing process,respectively.Some composite silicone rubber insulation boards were prepared and evaluated by the thermal conductivity and insulation performance.The results show that the product prepared by the kneading process has resulted in a reduced heat preservation ability of perlite,probably due to the broken hollow particles.The insulation board prepared with fumed silica as a main filler is difficult to form their shape,and the minimum thermal conductivity is 0.172 8 W·m?1·K?1 for the formed sample.When a mass ratio of perlite and fumed silica in silicone rubber is 37.5%and the product thickness is 2.5 cm,the minimum thermal conductivity is 0.034 9 W·m?1·K?1,and the back-side temperature is 67℃after heating at 250℃for 4 min,which basically meets the application requirements of thermal insulation materials for tobacco facility.
[1]金治国.一种真空隔热保温的加热不燃烧香烟全方位加热装置及其套件[P]. CN Patent, 201920602369.8, 2020?01?07.JIN Zhiguo. An omnidirectional heating device and its kit with vacuum heat insulation materials for heating non burning cigarette(in Chinese).CN Patent, 201920602369.8, 2020?01?07.
[2]韩敬美,郑绪东,汤建国,等.一种微型加热保温及散热装置[P].CN Patent, 201920835316.0, 2020?04?24.HAN Jingmei, ZHENG Xudong, TANG Jianguo, et al. A miniature heating, heat preservation and heat dissipation device(in Chinese). CN Patent, 201920835316.0, 2020?04?24.
[3]雷萍,汤建国,陈永宽,等.一种炭加热不燃烧卷烟用复合隔热材料[P]. CN Patent, 201821780293.X, 2019?10?29.LEI Ping, TANG Jianguo, CHEN Yongkuan, et al. A composite thermal insulation material for carbon heating non burning cigarettes(in Chinese). CN Patent, 201821780293.X, 2019?10?29.
[4]周瑾,廖桂民,宁琦,等.一种用于加热不燃烧烟草加热器的隔热件[P]. CN Patent, 201911391958.7, 2020?04?10.ZHOU Jing, LIAO Guiming, NING Qi, et al. A thermal insulation element for heating non burning tobacco heater(in Chinese). CN Patent, 201911391958.7, 2020?04?10.
[5]孙志坚,孙玮,傅加林,等.国内绝热保温材料现状及发展趋势[J].能源工程, 2001(4):26–28.SUN Zhijian, SUN Wei, FU Jialin, et al. Energy Engin(in Chinese),2001(4):26–28.
[6]曾珍,张雄.建筑保温材料的发展[J].上海建材, 2005, 4(4):28–30.ZENG Zhen, ZHANG Xiong. Shanghai Building Mater(in Chinese),2005, 4(4):28–30.
[7]倪德良,保温隔热材料(上)[J].节能与环保, 1989(3):13–19.NI Deliang. Jieneng yu Huanbao(in Chinese), 1989(3):13–19.
[8]瑚佩,姜勇刚,张忠明,等.耐高温、高强度隔热复合材料研究进展[J].材料导报, 2020, 34(7):86–94.HU Pei, JIANG Yonggang, ZHANG Zhongming, et al. Mater Rep(in Chinese), 2020, 34(7):86–94.
[9]江峰,江伟辉,冯果,等. SiO2气凝胶添加量对YSZ多孔隔热材料制备与性能的影响[J].中国陶瓷, 2020, 56(2):14–19.JIANG Feng, JIANG Weifeng, FENG Guo, et al. China Ceram(in Chinese), 2020, 56(2):14–19.
[10]史振宇. Zr O2气凝胶材料的微观结构调控及其隔热性能研究[D].浙江:浙江大学, 2018.SHI Zhengyu. Microstructure Control and Thermal Insulation Properties of ZrO2 Aerogel(in Chinese, dissertation). Hangzhou:Zhejiang University, 2018.
[11] MIAO C, LIANG L X, ZHANG F, et al. Review of the fabrication and application of porous materials from silicon-rich industrial solid waste[J]. Intern J Min Met Mater, 2022, 29(3):424–438.
[12] GAO H, LIU H, LIAO L, et al. Improvement of performance of foam perlite thermal insulation material by the design of a triple-hierarchical porous structure[J]. Energy Buildings, 2019, 200:21–30.
[13]张富新,谢海泉.珍珠岩尾砂资源化利用的技术条件分析[J].矿产综合利用, 2004(3):31–34.ZHANG Fuxin, XIE Haiquan. Multip Utiliz Min Res(in Chinese),2004(3):31–34.
[14] DAVRAZ M, KORU M, A, AKDAG E, et al. Investigating the use of raw perlite to produce monolithic thermal insulation material[J]. Constr Build Mater, 2020, 263(14):1–7.
[15]严育通,贾宝剑,周红升,等.珍珠岩矿床地质背景研究进展[J].信阳师范学院学报:自然科学版, 2016, 29(4):645–649.YAN Yutong, JIA Baojian, ZHOU Hongsheng, et al. J Xinyang Norm Univ:Nat Sci Ed(in Chinese), 2016, 29(4):645–649.
[16]张宪圆,林克辉,谢红波.国内外珍珠岩概述及其在建筑领域的应用分析[J].广东建材, 2012, 28(2):19–21.ZHANG Xianyuan, LIN Kehui, XIE Hongbo. Guangdong Jiancai(in Chinese), 2012, 28(2):19–21.
[17] WANG Z S, TU H C, GAO J X, et al. A novel building thermal insulation material:Expanded perlite modified by aerogel[J]. Adv Mater Res, 2011, 250–253:507–512.
[18] BENANE B, BAEZA G P, ZHAL B, et al. Multiscale structure of super insulation nano-fumed silicas studied by SAXS, tomography and porosimetry[J]. Acta Mater, 2019, 168:401–410.
[19] SHAFI S, TIAN J, NAVIK R, et al. Fume silica improves the insulating and mechanical performance of silica aerogel/glass fiber composite[J]. J Supercrit Fluids, 2019, 148:9–15.
[20] LIAN Tseng-Wen, KONDO Akira, KOZAWA Takahiro, et al. Effect of fumed silica properties on the thermal insulation performance of fibrous compact[J]. Ceram Inter, 2015, 41(8):9966–9971.
[21] TANG X Y, YU Y X. Preparation of fumed silica compacts for thermal insulation using wet processing method[J]. Int J Appl Ceram Tech,2018, 15(1):232–236.
[22] ZOU W, WANG X, YU W, et al. Opacifier embedded and fiber reinforced alumina-based aerogel composites for ultra-high temperature thermal insulation[J]. Ceram Inter, 2018, 45(1):644–650.
[23] RYU J S, OH K S, LEE B W. High performance of fumed silica insulation board for green building[J]. Adv Mater Research, 2013, 689:403–406.
[24] PAREDES M, ANGAMMANA C J, JAYARAM S H. In Experimental study of dielectric properties of fumed silica/silicone composites, 2016IEEE Conference on Electrical Insulation and Dielectric Phenomena(CEIDP), 2016:683–686.
[25]郭月,田晶,李晓雷,等.气相法二氧化硅在硅橡胶中的应用[J].辽宁化工, 2010, 39(3):242–244.GUO Yue, TIAN Jing, LI Xiaolei, et al. Liaoning Chem Ind(in Chinese), 2010, 39(3):242–244.
[26] ALQUDSI A Y, GHUNEM R A, DAVID E. A novel framework to study the role of ground and fumed silica fillers in suppressing DC erosion of silicone rubber outdoor insulation[J]. Energies, 2021, 14:1–15.
[27]姜水军,任瑞晨,张文军.珍珠岩超细粉体橡胶助剂的初步研究[J].有色矿冶, 2004, 20:117–120.JIANG Shuijun, REN Ruichen, ZHANG Wenjun. Non-Ferrous Min Met(in Chinese), 2004, 20:117–120.
[28]陈晓松,熊煦,刘日鑫,等.丁苯橡胶/膨胀珍珠岩复合材料的制备[J].硅酸盐通报, 2016, 35(5):1583–1587.CHEN Xiaosong, XIONG Xu, LIU rixin, et al. Bull Chin Ceram Soc(in Chinese), 2016, 35(5):1583–1587.
基本信息:
DOI：10.14062/j.issn.0454-5648.20220619
中图分类号:TB332;TQ333.93
引用信息:
[1]王威,孔波,陈淑梅,等.膨胀珍珠岩及气相二氧化硅填充硅橡胶复合材料的制备与隔热性能[J].硅酸盐学报,2023,51(04):975-981.DOI:10.14062/j.issn.0454-5648.20220619.
基金信息:
湖南中烟工业技术有限责任公司开放课题(KY2021KF0011); 湖南省大学生创新训练计划项目(S2022105330329)
2023-03-09
2023-03-09
2023-03-09