铌酸钠(NaNbO3)基无铅陶瓷具有超高的储能密度，在高功率介电储能电容器领域引起了广泛关注。然而，纯NaNbO3陶瓷在室温表现为矩形形状的类铁电电滞回线，并伴随着大的回滞和高的剩余极化强度，往往导致大的能量损耗。为优化NaNbO3的储能性能，基于相界调控策略采用传统固相法制备了(1–x)NaNbO3–xCaTiO3(0.08≤x≤0.18)陶瓷，并使用CuO作为助烧剂。结果表明，该体系在0.09≤x≤0.16范围内存在因晶体结构改变而引起的多晶型相界区域，其中相界组分0.84NaNbO3–0.16CaTiO3在590kV/cm时的最大极化强度为42.2μC/cm2，可逆储能密度达到6.1J/cm3，储能效率为77%。同时该陶瓷表现出良好的频率和温度稳定性，以及优异的放电性能。为铌酸钠基高性能储能电容器材料的开发提供了新思路。
Abstract：Introduction Lead-free sodium niobate (NaNbO3) based ceramics with a superior energy storage density have attracted recent attention in high power dielectric energy storage applications.However,a pure NaNbO3 (NN) ceramic exhibits a square-like square hysteresis loop associating with a large hysteresis and a high remnant polarization at room temperature,leading to a high energy dissipation.In general,stabilizing the antiferroelectricity in NN ceramic is one of the effective measures to solve the problems above.However,despite efforts are made on this measure,the large hysteresis is still kept due to the existence of antiferroelectricferroelectric phase transition.The compositions in the phase boundary region usually exhibit abnormally enhanced electrical properties and relaxation characteristics,thus constructing a phase boundary region in NN through composition modulation is another promising method.Moreover,sodium element volatilizes inevitably during the high-temperature and long-time sintering process,giving rise to a poor sintering quality in NN system,which is not beneficial to achieving superior energy storage performance.In this paper,(1–x)NaNbO3–x CaTiO3 (NN–CT100x,0.08≤x≤0.18) ceramics were prepared by a conventional solid-state method with CuO as a sintering aid.The phase structure and polymorphic phase boundary in NN–CT100x system were investigated,and the energy storage performance of compositions in the phase boundary region was analyzed.Materials and method For the synthesis of NN–CT100x powder,Na_2CO3 (≥99.8%,in mass fraction,the same below),Nb_2O5(≥99.9%),CaCO3 (≥99.0%),TiO2 (≥98.0%) and CuO (≥99.0%) were used as raw materials (Shanghai Sinopharm Chemical Reagent Co.,Ltd.,China).The raw materials were weighed/mixed according to the stoichiometric ratio and ground with anhydrous ethanol in a ball mill with zirconia balls for 12 h.After dried and sieved,the powder was calcined at 900℃for 6 h.The calcined powders were mixed with 1.5%(in mole fraction) of CuO as a sintering aid and further ground for 12 h.The ground powder was hand-pressed into discs with the diameter of 7 mm and the thickness of 1.2 mm and then further densified by cold isostatic pressing at300 MPa for 30 min.The NN–CT100x discs were sintered at 1 050–1 250℃for 2 h.Results and discussion Based on the results by X-ray diffraction,Raman spectroscopy and dielectric behavior,an‘antiferroelectric P phase (orthorhombic,Pbma)–ferroelectric INC phase–paraelectric CT phase (orthorhombic,Pbnm)’polymorphic phase boundary(PPB) region exists as 0.09≤x≤0.16 when CaTiO3 content increases.The polarization exhibits an enhancement in compositions within this PPB region.The optimum comprehensive energy storage performance is obtained as x=0.16,having the energy storage density (Wrec) of 3.04 J/cm3 and efficiency (?) of 84.4%at 300 kV/cm,respectively.The difference between the maximum polarization(Pm) and the remnant polarization (Pr) of the NN–CT16 ceramic increases as the electric field increases,thus obtaining an admirable energy storage performance.This composition is in the PPB region and contains a few antiferroelectric phases.These antiferroelectric phases are easily transformed into ferroelectric phases at high electric fields,which?reduces from 92.4%to 77.0%.The NN–CT16composition has a high Pm of 42.2μC/cm2,a high Wrec of 6.1 J/cm3 and?of 77%at 590 kV/cm.For the NN–CT16 ceramic,Wrec and?both exhibit a frequency stability at 1–300 Hz,with minimal variations of<10%and<8%,respectively.Furthermore,the Wrec and?also demonstrate temperature-insensitive characteristics at 25–160℃,with small variations of<10%and<5%,respectively.The discharge energy density (Wdis) of the NN–CT16 ceramic increases and reaches a plateau in a short time.The t0.9 (time at which 90%of the stored energy is released) is less than 8μs.Moreover,the t0.9 decreases with the increasing electric field or temperature,indicating the discharge rate accelerates,which is probably ascribed to domains respond quickly and switch more easily at high electric fields or high temperatures.Conclusions Based on the phase boundary modulation strategy,the NN–CT100x (0.08≤x≤0.18) ceramics were designed and prepared via introducing CaTiO3 into NN with CuO as a sintering aid.The polarization of the compositions in the phase boundary region was enhanced.The NN–CT16 ceramic exhibited a high maximum polarization of 42.2μC/cm2,a high energy storage density of 6.1 J/cm3 and an energy efficiency of 77%at 590 k V/cm.It also exhibited a good frequency/temperature stability and an excellent discharge performance.This ceramic could be used as a promising dielectric energy storage material.
[1] YANG L T, KONG X, LI F, et al. Perovskite lead-free dielectrics for energy storage applications[J]. Prog Mater Sci, 2019, 102:72–108.
[2] ZHANG L, PU Y P, CHEN M, et al. Design strategies of perovskite energy-storage dielectrics for next-generation capacitors[J]. J Eur Ceram Soc, 2023, 43(14):5713–5747.
[3]杨敏铮,江建勇,沈洋.高能量密度介电储能材料研究进展[J].硅酸盐学报, 2021, 49(7):1249–1262.YANG Minzheng, JIANG Jianyong, SHEN Yang. J Chin Ceram Soc,2021, 49(7):1249–1262.
[4] YANG Z T, DU H L, JIN L, et al. High-performance lead-free bulk ceramics for electrical energy storage applications:Design strategies and challenges[J]. J Mater Chem A, 2021, 9(34):18026–18085.
[5] HE Q F, SUN K, SHI Z C, et al. Polymer dielectrics for capacitive energy storage:From theories, materials to industrial capacitors[J].Mater Today, 2023, 68:298–333.
[6] CHE Z Y, MA L, LUO G G, et al. Phase structure and defect engineering in(Bi0.5Na0.5)TiO3-based relaxor antiferroelectrics toward excellent energy storage performance[J]. Nano Energy, 2022, 100:107484.
[7]杜金花,李雍,孙宁宁,等.无机电介质材料储能行为研究现状[J].硅酸盐学报, 2022, 50(3):608–624.DU Jinhua, LI Yong, SUN Ningning, et al. J Chin Ceram Soc, 2022,50(3):608–624.
[8] YANG D, GAO J, SHU L, et al. Lead-free antiferroelectric niobates AgNbO3 and Na NbO3 for energy storage applications[J]. J Mater Chem A, 2020, 8(45):23724–23737.
[9]王子瑄,李卓,张家勇,等. Na NbO3–CaZrO3–Bi0.5Na0.5Ti O3三元系陶瓷的相结构与储能性能[J].硅酸盐学报, 2023, 51(6):1530–1540.WANG Zixuan, LI Zhuo, ZHANG Jiayong, et al. J Chin Ceram Soc,2023, 51(6):1530–1540.
[10] CHEN J, FENG D. TEM study of phases and domains in NaNbO3 at room temperature[J]. Phys Status Solidi A, 1988, 109(1):171–185.
[11] XU Y H, HONG W, FENG Y J, et al. Antiferroelectricity induced by electric field in NaNbO3-based lead-free ceramics[J]. Appl Phys Lett,2014, 104(5):052903.
[12] ZHANG M H, ZHAO C H, FULANOVI?L, et al. Revealing the mechanism of electric-field-induced phase transition in antiferroelectric NaNbO3 by in situ high-energy X-ray diffraction[J].Appl Phys Lett, 2021, 118(13):132903.
[13] QI H, ZUO R Z. Evolving antiferroelectric stability and phase transition behavior in NaNbO3–BaZrO3–CaZrO3 lead-free ceramics[J].J Eur Ceram Soc, 2019, 39(7):2318–2324.
[14] SHIMIZU H, GUO H Z, REYES-LILLO S E, et al. Lead-free antiferroelectric:x Ca Zr O3–(1–x)Na Nb O3 system(0≤x≤0.10)[J]. Dalton Trans, 2015, 44(23):10763–10772.
[15] LIU Z Y, LU J S, MAO Y Q, et al. Energy storage properties of Na NbO3–CaZrO3 ceramics with coexistence of ferroelectric and antiferroelectric phases[J]. J Eur Ceram Soc, 2018, 38(15):4939–4945.
[16] CHEN Z G, MAO S F, MA L, et al. Phase engineering in NaNbO3antiferroelectrics for high energy storage density[J]. J Materiomics,2022, 8(4):753–762.
[17] LUO N N, HAN K, CABRAL M J, et al. Constructing phase boundary in AgNbO3 antiferroelectrics:Pathway simultaneously achieving high energy density and efficiency[J]. Nat Commun, 2020, 11(1):4824.
[18]周明星.铌酸钠基无铅铁电陶瓷的制备、结构及性能研究[D].北京:中国科学院大学, 2020.ZHOU Mingxing. Study on preparation, structure and properties of sodium niobate-based lead-free ferroelectric ceramics[D]. Beijing:University of Chinese Academy of Sciences, 2020.
[19]祁核.铌酸钠基准同型无铅压电陶瓷的介电弛豫调控、机电性能及其结构机理研究[D].合肥:合肥工业大学, 2017.QI He. Study on dielectric relaxation regulation, electromechanical properties and structural mechanism of sodium niobate-based lead-free piezoelectric ceramics[D]. Hefei:Hefei University of Technology, 2017.
[20] FU J, ZUO R Z, WANG X H, et al. Phase transition characteristics and piezoelectric properties of compositionally optimized alkaline niobate based ceramics[J]. J Alloys Compd, 2009, 486(1/2):790–794.
[21] GUO H Z, SHIMIZU H, MIZUNO Y, et al. Strategy for stabilization of the antiferroelectric phase(Pbma)over the metastable ferroelectric phase(P21ma)to establish double loop hysteresis in lead-free(1–x)NaNbO3–x SrZrO3 solid solution[J]. J Appl Phys, 2015, 117(21):214103.
[22] GAO L S, GUO H Z, ZHANG S J, et al. A perovskite lead-free antiferroelectric x Ca HfO3–(1–x)NaNbO3 with induced double hysteresis loops at room temperature[J]. J Appl Phys, 2016, 120(20):204102.
[23] GAO L S, GUO H Z, ZHANG S J, et al. Stabilized antiferroelectricity in x BiScO3–(1–x)NaNbO3 lead-free ceramics with established double hysteresis loops[J]. Appl Phys Lett, 2018, 112(9):092905.
[24] YE J M, WANG G S, CHEN X F, et al. Effect of rare-earth doping on the dielectric property and polarization behavior of antiferroelectric sodium niobate-based ceramics[J]. J Materiomics, 2021, 7(2):339–346.
[25] ZHOU H Y, LIU X Q, ZHU X L, et al. CaTiO3 linear dielectric ceramics with greatly enhanced dielectric strength and energy storage density[J]. J Am Ceram Soc, 2018, 101(5):1999–2008.
[26] NIKOLI?J, PAVI?L,?ANTI?A, et al. Novel insights into electrical transport mechanism in ionic-polaronic glasses[J]. J Am Ceram Soc,2018, 101(3):1221–1235.
[27] KIM C, PILANIA G, RAMPRASAD R. From organized highthroughput data to phenomenological theory using machine learning:the example of dielectric breakdown[J]. Chem Mater, 2016, 28(5):1304–1311.
[28] TRIPATHI S, PANDEY D, MISHRA S K, et al. Morphotropic phase-boundary-like characteristic in a lead-free and non-ferroelectric(1–x)NaNbO3–x Ca TiO3 system[J]. Phys Rev B, 2008, 77(5):052104.
[29] SHI R K, PU Y P, WANG W, et al. A novel lead-free Na NbO3–Bi(Zn0.5Ti0.5)O3 ceramics system for energy storage application with excellent stability[J]. J Alloys Compd, 2020, 815:152356.
[30] HUSSAIN A, NAWAZ S, JABEEN N, et al. Enhanced ferroelectric and piezoelectric response by MnO2 added Bi0.5(K0.2Na0.8)0.5Ti O3ceramics[J]. J Solid State Chem, 2022, 306:122716.
[31]李明阳,曹嘉宁,王梦凯,等. Bi2O3掺杂对Na NbO3无铅陶瓷储能性能的研究[J].黄河科技学院学报, 2022, 24(11):26–29.LI Mingyang, CAO Jianing, WANG Mengkai, et al. J Huanghe S&T Coll, 2022, 24(11):26–29.
[32] LUO G G, ZHUANG D Y, YANG K H, et al. Enhanced comprehensive energy storage properties in Na NbO3-based relaxor antiferroelectric via MnO2 modification[J]. J Mater Sci Mater Electron,2023, 34(18):1444.
[33] LI X H, JIANG M, LIU J, et al. Phase transitions and electrical properties of(1-x)(K0.5Na0.5)NbO3-x BiScO3 lead-free piezoelectric ceramics with a CuO sintering aid[J]. Phys Status Solidi A, 2009,206(11):2622–2626.
[34] JAIN A, WANG Y G, WANG N, et al. Critical role of CuO doping on energy storage performance and electromechanical properties of Ba0.8Sr0.1Ca0.1Ti0.9Zr0.1O3 ceramics[J]. Ceram Int, 2020, 46(11):18800–18812.
[35] DOU M X, FU J, ZUO R Z. Electric field induced phase transition and accompanying giant poling strain in lead-free NaNbO3–BaZrO3ceramics[J]. J Eur Ceram Soc, 2018, 38(9):3104–3110.
[36] QI H, XIE A W, FU J, et al. Emerging antiferroelectric phases with fascinating dielectric, polarization and strain response in NaNbO3–(Bi0.5Na0.5)TiO3 lead-free binary system[J]. Acta Mater,2021, 208:116710.
[37] XIE A W, FU J, ZUO R Z, et al. NaNbO3–CaTiO3 lead-free relaxor antiferroelectric ceramics featuring giant energy density, high energy efficiency and power density[J]. Chem Eng J, 2022, 429:132534.
[38] TRIPATHI S, MISHRA S K, KRISHNA P S R, et al. Morphotropic phase transition in a lead-free system(1–x)NaNbO3–x Ca TiO3[J]. Acta Cryst Sect A, 2011, 67(a1):C672.
[39] SHAKHOVOY R A, RAEVSKAYA S I, SHAKHOVAYA L A, et al.Ferroelectric Q and antiferroelectric P phases’ coexistence and local phase transitions in oxygen-deficient Na NbO3 single crystal:Micro-Raman, dielectric and dilatometric studies[J]. J Raman Spectrosc, 2012, 43(8):1141–1145.
[40] GE G L, SHI C, CHEN C K, et al. Tunable domain switching features of incommensurate antiferroelectric ceramics realizing excellent energy storage properties[J]. Adv Mater, 2022, 34(24):2201333.
[41] WANG X J, WANG X Z, HUAN Y, et al. A combined optimization strategy for improvement of comprehensive energy storage performance in sodium niobate-based antiferroelectric ceramics[J].ACS Appl Mater Interfaces, 2022, 14(7):9330–9339.
[42] WEI K, DUAN J H, ZHOU X F, et al. Achieving ultrahigh energy storage performance for Na NbO3-based lead-free antiferroelectric ceramics via the coupling of the stable antiferroelectric R phase and nanodomain engineering[J]. ACS Appl Mater Interfaces, 2023, 15(41):48354–48364.
[43]黄佳佳,张勇,陈继春.高储能密度介电材料研的究进展[J].材料导报, 2009, 23(增刊1):307–312.HUANG Jiajia, ZHANG Yong, CHEN Jichun. Mater Rep, 2009,23(Suppl 1):307–312.
[44] LIU W F, REN X B. Large piezoelectric effect in Pb-free ceramics[J].Phys Rev Lett, 2009, 103(25):257602.
[45] LIU W B, ZHENG T, RUAN X Z, et al. Synergy of lead vacancies and morphotropic phase boundary to promote high piezoelectricity and temperature stability of PBZTN ceramics[J]. J Mater Sci Technol,2023, 137:1–7.
[46] XU R, XU Z, FENG Y J, et al. Evaluation of discharge energy density of antiferroelectric ceramics for pulse capacitors[J]. Appl Phys Lett,2016, 109(3):032903.
基本信息:
DOI：10.14062/j.issn.0454-5648.20230858
中图分类号:TQ174.1;TM534.1
引用信息:
[1]常凡,罗庚光,罗能能.铌酸钠基陶瓷的相界调控及储能性能[J].硅酸盐学报,2024,52(04):1392-1402.DOI:10.14062/j.issn.0454-5648.20230858.
基金信息:
国家自然科学基金面上项目(52072080);; 广西杰出青年基金项目(2022GXNSFFA035034)
2024-03-09
2024-03-09
2024-03-09