通过开展超高性能混凝土(UHPC)基体的再水化试验,测试了不同再水化时间水泥石的化学结合水量、试件膨胀率和抗压强度,基于Krstulovi?–Dabi?的水泥水化动力学和水泥水化微观信息,建立了再水化模型,同时结合微观形貌变化和孔结构变化,基于建立的模型,分析了再水化作用对其水稳定性的影响机理。结果表明:在低水灰比(0.15～0.30)范围内,水灰比越低,再水化结合水量在前期越大,后期反而越小;再水化过程中,试件膨胀率随水灰比的降低呈增大趋势;不同水灰比水泥石的抗压强度随再水化时间的增长呈增大和减小交替出现的趋势。根据再水化模型计算的水泥水化度模型预测结果和试验结果吻合良好,表明所建立的模型可以较准确地模拟UHPC基体的再水化过程。水灰比0.30水泥石较大的水泥水化速率导致其具有较高的抗压强度增长幅度。再水化前期,水泥水化速率快,再水化产物不断填补水泥石内部初始孔隙,后期水泥水化速率缓慢,再水化产物体积膨胀导致水泥石出现微裂缝,UHPC基体性能劣化。
Abstract：A rehydration test of ultra-high performance concrete(UHPC) matrix was conducted to measure the chemically bound water contents, specimen expansion ratios, and compressive strengths of hardened cement pastes at different rehydration time, and the rehydration model was proposed based on the Krstulovi?–Dabi? hydration dynamics of cement and microstructure information of cement hydration. The mechanism regarding the rehydration effect on the water stability was discussed, and the microscopic appearance change with pore structure change was analyzed based on the proposed model. The results show that the bound water content of rehydration increases during the early period but decreases during the late period as the water-cement ratio decreases from 0.30 to 0.15. The specimen expansion ratio increases as the water-cement ratio decreases during the rehydration process. The compressive strength of hardened cement pastes at different water-cement ratios has an alternating tendency of increasing and decreasing with the increase of rehydration time. The simulated data by the model are in good agreement with the experimental results, indicating that the proposed model can accurately simulate the rehydration process of UHPC matrix. The increased scope of compressive strength of hardened cement paste with the water-cement ratio of 0.30 is greater due to its higher hydration rate of cement. During the early period of rehydration, a hydration rate of cement becomes greater, and the rehydration products gradually fill in the initial pores of hardened cement paste. However, during the late period of rehydration, a hydration rate of cement is lower, and the rehydration products cause some microcracks of hardened cement paste due to its volume expansion, resulting in the degradation of properties of UHPC matrix.
[1] LEE N K, KOH K T, KIM M O, et al. Uncovering the role of micro silica in hydration of ultra-high performance concrete(UHPC)[J]. Cem Concr Res, 2018, 104:68-79.
[2] LIN Y Z, YAN J C, WANG Z F, et al. Effect of silica fumes on fluidity of UHPC:Experiments, influence mechanism and evaluation methods[J]. Constr Build Mater, 2019, 210:451-460.
[3] TAFRAOUI A, ESCADEILLAS G, LEBAILI S, et al. Metakaolin in the formulation of UHPC[J]. Constr Build Mater, 2009, 23(2):669-674.
[4] SCIVENNER K, QUZIA A, JUILLAND P, et al. Advances in understanding cement hydration mechanisms[J]. Cem Concr Res, 2019,124:1-16.
[5] AN M Z, WANG Y, YU Z R. Damage mechanisms of ultra-high-performance concrete under freeze-thaw cycling in salt solution considering the effect of rehydration[J]. Constr Build Mater,2019, 198:546-552.
[6]罗玲玲.再水化作用对低水灰比水泥基材料性能的影响研究[D].北京:北京交通大学, 2018.LUO Lingling. Effect of rehydration on properties of cement-based materials with low water-cement ratio(in Chinese, dissertation).Beijing:Beijing Jiaotong University, 2018.
[7]葛晓丽,刘加平,王育江,等.未水化水泥颗粒后期水化对UHPC性能的影响[J].土木建筑与环境工程, 2016, 38(1):40-45.GE Xiaoli, LIU Jiaping, WANG Yujiang, et al. J Civ Archit Environ Eng(in Chinese), 2016, 38(1):40-45.
[8] HUANG H L, YE G, DAMIDOT D. Characterization and quantification of self-healing behaviors of microcracks due to further hydration in cement paste[J]. Cem Concr Res, 2013, 52(10):71-81.
[9] HUANG H L, Ye G, PEL L. New insights into autogenous self-healing in cement paste based on nuclear magnetic resonance(NMR)tests[J].Mater Struct, 2016, 49(7):2509-2524.
[10] ZHU Y, YANG Y Z, YAO Y. Autogenous self-healing of engineered cementitious composites under freeze-thaw cycles[J]. Constr Build Mater, 2012, 34:522-530.
[11]杨雷,管学茂.混凝土中未水化水泥后期水化的危害研究[J].水泥工程, 2004(3):8-11.YANG Lei, GUAN Xuemao. Cem Eng(in Chinese), 2004(3):8-11.
[12] WANG Y, AN M Z, YU Z R, et al. Impacts of various factors on the rehydration of cement-based materials with a low water-binder ratio using mathematical models[J]. Constr Build Mater, 2016, 125:160-167.
[13]管学茂,杨雷,姚燕.低水灰比高性能混凝土的耐久性研究[J].混凝土, 2004(10):3-4, 24.GUAN Xuemao, YANG Lei, YAO Yan. Concrete(in Chinese),2004(10):3-4, 24.
[14] HILLEMEIER B, SCHRODER M. Poor durability of high performance concrete with water cement ratio<0.3[A]//Durability of High Performance Concrete, Proc. RILEM Workshop[C], Cachan,France, 1995:70-75.
[15]阎培渝,覃肖,杨文言.大体积补偿收缩混凝土中钙矾石的分解与二次生成[J].硅酸盐学报, 2000, 28(4):319-324.YAN Peiyu, QIN Xiao, YANG Wenyan. J Chin Ceram Soc, 2000,28(4):319-324.
[16] ZENG Qiang, LI Kefei, FEN-CHONG T, et al. Determination of cement hydration and pozzlanic reaction extents for fly-ash cement pastes[J]. Constr Build Mater, 2012, 27(1):560-569.
[17] LAWRENCE P, CYR M, RINGOT E. Mineral admixtures in mortars:effects of insert materials on short-term hydration[J]. Cem Concr Res,2003, 33(12):1939-1947.
[18] LGARASHI S I, KUBO H R, KAWAMURA M. Long-term volume changes and microcracks formation in high strength mortars[J]. Cem Concr Res, 2000, 30(6):943-951.
[19]刘建忠,孙伟,缪昌文,等.矿物掺合料对低水胶比混凝土干缩和自收缩的影响[J].东南大学学报(自然科学版), 2009, 39(3):580-585.LIU Jianzhong, SUN Wei, MIAO Changwen, et al. J Southeast Univ:Nat Sci Ed(in Chinese), 2009, 39(3):580-585.
[20]王培铭,彭宇,刘贤萍.聚合物改性水泥水化程度测定方法比较[J].硅酸盐学报, 2013, 41(8):1116-1123.WANG Peiming, PENG Yu, LIU Xianping. J Chin Ceram Soc, 2013,41(8):1116-1123.
[21] PAPADAKIS V G. Experimental investigation and theoretical modeling of silica fume activity in concrete[J]. Cem Concr Res, 1999,29(1):79-86.
[22]葛晓丽.低水胶比水泥基材料的水稳定性及机理[D].重庆:重庆大学, 2017.GE Xiaoli. The water stability and mechanism of low water binder ratio cement based materials(in Chinese, dissertation). Chongqing:Chongqing University, 2017.
[23] MILLER M, BOBKO C, VANDAMME M, et al. Surface roughness criteria for cement paste nanoindentation[J]. Cem Concr Res, 2008,38(4):467-476.
[24] ACKER P. Micromechanical analysis of creep and shrinkage mechanisms//Proceedings of the Sixth International Conference CONCREEP6:Creep, Shrinkage and Durability Mechanics of Concrete and Other Quasi-Brittle Materials[C], Oxford, UK, 2001:15-25.
[25] PARK K B, NOGUCHI T, PLAWSKY J. Modeling of hydration reactions using neural networks to predict the average properties of cement paste[J]. Cem Concr Res, 2005, 35(9):1676-1684.
[26]金贤玉,王宇纬,田野，等.基于微观信息的水泥水化动力学模型研究[J].建筑材料学报, 2014, 17(5):862-867.JIN Xianyu, WANG Yuwei, TIAN Ye, et al. J Build Mater(in Chinese), 2014, 17(5):862-867.
[27]田野.复掺矿物掺合料混凝土性能及抗裂机理、微观特性研究[D].杭州:浙江大学, 2007.TIAN Ye. Investigation on the performance, cracking mechanism and micro-properties of concrete incorporated with mineral admixtures(in Chinese, dissertation). Hangzhou:Zhejiang University, 2007.
[28] DABI?P, KRSTULOVI?R, RU?I?D. A new approach in mathematical modelling of cement hydration development[J]. Cem Concr Res. 2000, 30(7):1017-1021.
[29]郭明磊,肖佳,左胜浩.水泥-石灰石粉胶凝材料孔结构多重分形特征以及与渗透性的关系[J].硅酸盐学报, 2019, 47(5):617-624.GUO Minglei, XIAO Jia, ZUO Shenghao. J Chin Ceram Soc, 2019,47(5):617-624.
[30] ZENG Q, LUO M Y, PANG X Y, et al. Surface fractal dimension:an indicator to characterize the microstructure of cement-based porous materials[J]. Appl Surf Sci, 2013, 282:302-307.
[31] TAZAWA E, MIYAZAWA S. Experimental study on mechanism of autogenous shrinkage of concrete[J]. Cem Concr Res, 1995, 25(8):1633-1638.
[32] TAZAWA E, MIYAZAWA S. Tensile and flexural strength of cement mortar subjected to non-uniform self-stress[J]. Mag Concr Res, 1992,44(161):241-248.
[33]王冲,王勇威,蒲心诚,等.超低水胶比水泥混凝土的自收缩特性及其机理[J].建筑材料学报, 2010(1):79-83.WANG Chong, WANG Yongwei, PU Xincheng, et al. J Build Mater(in Chinese), 2010(1):79-83.
[34]刘丹.不同养护制度下活性粉末混凝土早期收缩的模型研究[D].北京:北京交通大学, 2017.LIU Dan. Research on the early-age shrinkage model of reactive powder concrete in different curing conditions(in Chinese,dissertation). Beijing:Beijing Jiaotong University, 2017.
[35]王月.氯盐冻融循环与侵蚀作用下活性粉末混凝土的耐久性研究[D].北京:北京交通大学,2016.WANG Yue. Durability of reactive powder concrete under the action of chloride salt freeze-thaw cycling and erosion(in Chinese,dissertation). Beijing:Beijing Jiaotong University, 2016.
基本信息:
DOI：10.14062/j.issn.0454-5648.20200214
中图分类号:TU528
引用信息:
[1]安明喆,刘亚州,张戈,等.再水化作用对超高性能混凝土基体显微结构和水稳定性的影响[J].硅酸盐学报,2020,48(11):1722-1731.DOI:10.14062/j.issn.0454-5648.20200214.
基金信息:
国家自然科学基金(51578049);; 中央高校基本科研业务费专项资金(2018YJS111)
2020-09-18
2020-09-18
2020-09-18