以ZrO2和Ta2O5粉体为原料,采用固相反应法制备了ZrO2掺杂Ta2O5陶瓷。研究了ZrO2掺杂对Ta2O5陶瓷的相组成、微观结构、抗弯强度、热膨胀系数和抗热震性能的影响。结果表明:ZrO2掺杂可在烧成过程中抑制β-Ta2O5相向α-Ta2O5相的转变,5%(质量分数,下同)ZrO2掺杂Ta2O5陶瓷为β-Ta2O5单相固溶体。3%ZrO2掺杂,显著抑制了Ta2O5陶瓷高温烧结过程中的晶粒长大,避免了晶界开裂;掺杂量达到5%以上时,可显著促进Ta2O5陶瓷的烧结致密化。5%ZrO2掺杂的Ta2O5陶瓷表现出较高的抗弯强度(74.5MPa),低的热膨胀系数(1.96×10-6/℃)和良好的抗热震性能。
Abstract：Ta2O5 ceramics doped with ZrO2 were prepared through solid-state reaction using Ta2O5 and ZrO2 micro-powders as raw materials. The effects of ZrO2 addition on the properties of Ta2O5 ceramics,such as phase composition,microstructure,bending strength,thermal expansion coefficient and thermal shock resistance,were investigated. The results show that the phase transformation for Ta2O5 ceramic from the orthorhombic (β) phase to the tetragonal (α) phase is inhibited by the introduction of ZrO2,and the Ta2O5 ceramic with 5% in mass ZrO2 doping is composed of pure β-Ta2O5 solid solution. With the addition of 3% ZrO2,the grain growth of Ta2O5 ceramic during sintering can be inhibited,and the cracking along grain boundary can be obviously avoided. The densification of Ta2O5 ceramic can be greatly improved when the amount of ZrO2 doped is more than 5%. The 5% ZrO2 doped Ta2O5 ceramic has high bending strength (74.5 MPa),a low thermal expansion coefficient(1.96 × 10-6/ ℃ ) and good thermal shock resistance.
[1]WU S,CHAN H M,HARMER M P.Effect of alumina additions on microstructural aspects of theβtoαtransformation in tantalum(V)oxide[J].J Am Ceram Soc,2005,88(9):2369-2373.
[2]RAMOS F E V,SAMARANCH B,HOMS N,et al.Pt/Ta2O5-ZrO2catalysts for vapour phase selective hydrogenation of crotonaldehyde[J].Appl Catal A:Gen,2008,349:165-169.
[3]MOLDOVAN M,WEYANT C M,JOHNSON D L,et al.Tantalum oxide coatings as candidate environmental barriers[J].J Therm Spray Technol,2004,13(1):51-56.
[4]SAMARANCH B,CLET G,HOUALLA M,et al.Synthesis and char-acterization of Ta2O5-ZrO2systems:structure,surface Acidity,and catalytic properties[J].Chem Mater,2007,19:1445-1451.
[5]YAMAGUCHI O,TOMIHISA D.Formation and transformation ofδ-Ta2O5solid solution in the system Ta2O5-Al2O3[J].J Am Ceram Soc,1987,70(11):335-338.
[6]ROTH R S,WARING J L,BROWER W S.Effect of oxide additions on the polymorphism of tantalum pentoxide:I.stabilization of the high temperature structure type[J].J Res Natl Bur Stand,1970,74(4):477-84.
[7]WU S,CHAN H M,HARMER M P.Compositional tailoring of the thermal expansion coefficient of tantalum(V)oxide[J].J Mater Sci,2006,41:689-695.
[8]CAVA R J,PECK W F,KRAJEWSKI J J.Enhancement of the dielec-tric constant of Ta2O5through substitution with TiO2[J].Nature,1995,377:215-8.
[9]GUO R,JIANG Y,BHALLA A S.Processing and annealing conditions on the dielectric properties of(Ta2O5)0.92(TiO2)0.08ceramics[J].Mater Lett,2002,57:270-274.
[10]BRENNECKA G L,PAYNE D A,SARIN P,et al.Phase transforma-tions in the high-temperature form of pure and TiO2-stabilized Ta2O5[J].J Am Ceram Soc,2007,90(9):2947-2953.
[11]LIU X,HUANG Y,YANG J.Effect of rheological properties of the suspension on the mechanical strength of Al2O3-ZrO2composites pre-pared by gelcasting[J].Ceram Int,2002,28(2):159-164.
[12]ZHANG X,LI W,HONG C,et al.A novel development of ZrB2/ZrO2functionally graded ceramics for ultrahigh-temperature application[J].Scr Mater,2008,59(11):1214-1217.
[13]CAVA R J,KRAJEWSKI J J.Dielectric properties of Ta2O5-ZrO2polycrystalline ceramics[J].J Appl Phys,1998,83(3):1613-1616.
[14]LEVIN E M,ROBBINS C R,MCMURDIE H F,Phase Diagram for Ceramist[M].New York:The American Ceramic Society,1979:p114.
[15]关振铎,张中太,焦金生.无机材料物理性能[M].北京:清华大学出版社,1992:162-163.GUAN Zhenduo,ZHANG Zhongtai,JIAO Jinseng.Physical Proper-ties of Inorganic Materials(in Chinese).Beijing:Tsinghua University press,1992:162-163.
基本信息:
DOI：10.14062/j.issn.0454-5648.2010.08.027
中图分类号:TQ174.1
引用信息:
[1]周健儿,王建东,张小珍,等.添加ZrO_2对Ta_2O_5陶瓷结构与性能的影响[J].硅酸盐学报,2010,38(08):1499-1502.DOI:10.14062/j.issn.0454-5648.2010.08.027.
基金信息:
江西省科技支撑计划资助项目
2010-08-15
2010-08-15