与氧化物透波陶瓷相比，氮化物透波陶瓷具有更加优异的耐高温性能，是最有希望满足高马赫数飞行器使用需求的高温透波材料。先驱体转化法具有加工成型温度低、可塑成型等优点，是制备氮化物高温透波陶瓷的主流方法。本文主要总结了近年来氮化物透波陶瓷先驱体方面的研究进展，主要涉及氮化硅、氮化硼、硅硼氮和硅氮氧等氮化物透波陶瓷先驱体的合成，以及通过热解转化制备目标陶瓷研究，并展望了今后应该重点关注的研究方向。
Abstract：High Mach precision guided aircraft has the important advantages of successful penetration with high level,presenting a strategic deterrent force to safeguard national core interests and maintain world peace.Its extremely high flight speed (>5 Ma) is an important guarantee of breakthrough capability,but causing severe aerodynamic erosion,heating,and ablation.Thus,it is a serious challenge to the communication,precise guidance,detonation and other combat tasks of the front-end antenna cover and antenna window.Therefore,the development of high-temperature transparent materials for antenna covers/windows that integrate various functions such as load-bearing,high-temperature resistance,and wave transmission is an urgent bottleneck problem to be solved.High temperature resistance is an important indicator of transparent materials.The service speed of low-speed aircraft is low,and organic transparent materials such as phenolic resin and epoxy resin with lower temperature resistance can meet the usage requirements.With the continuous improvement of aircraft flight speed,higher temperature requirements are also expected for the use of transparent materials.The selection of transparent materials has transitioned from organic polymer systems to inorganic ceramic systems.Traditional inorganic transparent ceramics mainly include oxide ceramics such as quartz and glass-ceramics,with short-term usage temperatures around 1 000℃.With the development of aircraft flight speed towards high Mach numbers,there is a higher demand for the high-temperature resistance of transparent ceramic materials.Nitride ceramics,represented by silicon nitride (Si—N),boron nitride (B—N),silicon boron nitrogen (Si—B—N),and silicon nitrogen oxide (Si—N—O),exhibit superior high-temperature resistance than oxide ceramics.They are the most promising high-temperature transparent materials to meet the requirements of high Mach number aircraft and have become a research hotspot both domestically and internationally.In recent years,researchers have conducted a detailed review of the research progress on nitride high-temperature transparent ceramic materials,which are a type of inorganic materials bonded by strong covalent bonds.They have the characteristics of high brittleness,high melting point and high hardness.Most nitride ceramics undergo obvious thermal decomposition reactions before melting,making it more difficult to sintering compared to carbide and boride ceramics.Typical sintering methods such as hot pressing or pressureless sintering have obvious shortcomings when preparing complex and precise structure antenna covers.The precursor conversion method has the advantages of low processing temperature,controllable composition,easy processing and plasticity,and has become the preferred method for the preparation of high-performance antenna covers.The precursor conversion method first requires the synthesis of organic polymers containing target ceramic elements,which can be transformed into target ceramics after high-temperature (>1 000℃) pyrolysis.By utilizing the soluble and fusible properties of polymers,it is possible to prepare complex and precise antenna radomes through close prototyping.At present,the development of new equipment is increasingly urgent for the precursor of nitride transparent ceramics,and the performance indicators of the precursor are also clearer.Driven by demand,systematic research has been carried out both domestically and internationally on the synthesis,transformation,and applications of nitride wave transmitting ceramic precursors.This not only provides rich material selection schemes for the development of high-temperature performance antenna covers,but also greatly enriches the development of precursor ceramics.This review mainly summarized the research progress in the precursor of nitride wave transmission ceramics in recent years,involving silicon nitride,boron nitride,silicon nitrogen oxide and other nitride wave transmission ceramic precursors,and proposes research directions in the future.It is expected that the work can provide certain reference for relevant researchers,and also look forward to more researchers paying attention to the research of nitride wave transmission precursors,supporting the development of wave transparent materials at high temperature.Summary and Prospects Compared with oxide ceramics for wave transparent,nitride ceramics with better high-temperature resistance are the most promising high-temperature wave transparent materials to meet the needs of high Mach number aircraft.Polymer-derived method presenting the advantages of low processing temperature and plasticity,is the promising method for preparing nitride ceramics for the wave transparent at high temperature.This review mainly summarized the research progress on the precursor of nitride wave transmitting ceramics in recent years,involving the synthesis of precursors for ceramics such as silicon nitride,boron nitride,silicon boron nitrogen,and silicon nitrogen oxide,as well as the preparation of target ceramics through thermal decomposition conversion.It also looks forward to the research directions in the future.
[1]蔡德龙,陈斐,何凤梅,等.高温透波陶瓷材料研究进展[J].现代技术陶瓷, 2019, 40(增刊1):4–120.CAI Delong, CHEN Fei, HE Fengmei, et al. Adv Ceram, 2019, 40(S1):4–120.
[2]崔雪峰,李建平,李明星,等.氮化物基陶瓷高温透波材料的研究进展[J].航空材料学报, 2020, 40(1):21–34.CUI Xuefeng, LI Jianping, LI Mingxing, et al. J Aeronaut Mater, 2020,40(1):21–34.
[3] ASIM M, SABA N, JAWAID M, et al. A review on phenolic resin and its composites[J]. Curr Anal Chem, 2018, 14(3):185–197.
[4]王贤明,李文,李航,等. GO/Si3N4改性环氧树脂涂层防腐透波性能研究[J].表面技术, 2021, 50(5):303–314.WANG Xianming, LI Wen, LI Hang, et al. Surf Technol, 2021, 50(5):303–314.
[5] ZHAO Z, ZHOU G X, YANG Z H, et al. Direct ink writing of continuous SiO2 fiber reinforced wave-transparent ceramics[J]. J Adv Ceram, 2020, 9(4):403–412.
[6] PETERS P W M, DANIELS B, CLEMENS F, et al. Mechanical characterisation of mullite-based ceramic matrix composites at test temperatures up to 1 200℃[J]. J Eur Ceram Soc, 2000, 20(5):531–535.
[7] LI D X, JIA D C, YANG Z H, et al. Principles, design, structure and properties of ceramics for microwave absorption or transmission at high-temperatures[J]. Int Mater Rev, 2022, 67(3):266–297.
[8] SUZDAL’TSEV E I. Radio-transparent ceramics:Yesterday, today,tomorrow[J]. Refract Ind Ceram, 2015, 55(5):377–390.
[9] ZHOU J, YE F, CHENG L F, et al. Development of high-temperature wave-transparent nitride-based CFCMCs for aircraft radomes[J].Compos Part A Appl Sci Manuf, 2023, 167:107444.
[10] HU X, SHAO C W, WANG J, et al. Characterization and high-temperature degradation mechanism of continuous silicon nitride fibers[J]. J Mater Sci, 2017, 52(12):7555–7566.
[11] LONG X, SHAO C W, WANG J, et al. High-temperature microstructural evolution of SiCN fibers derived from polycarbosilane with different C/N ratios[J]. J Eur Ceram Soc, 2020, 40(3):622–629.
[12] THIYAGARAJAN G B, DEVASIA R. Simple and low-cost synthetic route for SiBCN ceramic powder from a boron-modified cyclotrisilazane[J]. J Am Ceram Soc, 2019, 102(1):476–489.
[13] NGUYEN T T, MUKHOPADHYAY T K, MACMILLAN S N, et al.Synthesis of aminosilane chemical vapor deposition precursors and polycarbosilazanes through manganese-catalyzed Si–N dehydrocoupling[J]. ACS Sustainable Chem Eng, 2022, 10(13):4218–4226.
[14] HOU Y B, LI B, SHAO C W, et al. Effect of high-temperature annealing in air and N2 atmosphere on the mechanical properties of Si3N4 fibers[J]. Mater Sci Eng A, 2018, 724:502–508.
[15] LI D, ZHANG C R, LI B, et al. Effects of heat treatment on properties of boron nitride fiber[J]. Sci China Technol Sci, 2012, 55(5):1376–1380.
[16] LONG X, SHAO C W, WANG Y D. Effects of boron content on the microwave-transparent property and high-temperature stability of continuous SiBN fibers[J]. J Am Ceram Soc, 2020, 103(8):4436–4444.
[17] LONG X, SHAO C W, WANG Y D. The formation of chemical/structural gradients in strong covalent bonded SiBN fibers under active nitrogen atmosphere[J]. J Eur Ceram Soc, 2021, 41(6):3333–3340.
[18] LONG X, WU Z Y, SHAO C W, et al. High-temperature oxidation behavior of SiBN fibers in air[J]. J Adv Ceram, 2021, 10(4):768–777.
[19] PENG Y Q, HAN K Q, ZHAO X, et al. Large-scale preparation of SiBN ceramic fibres from a single source precursor[J]. Ceram Int, 2014,40(3):4797–4804.
[20] HU X, SHAO C W, WANG J, et al. Effects of residual radicals on compositional and structural stability of silicon nitride fibers[J]. J Eur Ceram Soc, 2017, 37(15):4497–4503.
[21] SEYFERTH D, WISEMAN G H, PRUD’HOMME C. A liquid silazane precursor to silicon nitride[J]. J Am Ceram Soc, 1983, 66(1):13–14.
[22] ARAI M, FUNAYAMA O, NISHII H, et al. High-purity silicon nitride fibers:US4818611[P]. 1989–04–04.
[23] FUNAYAMA O, ARAI M, TASHIRO Y, et al. Tensile strength of silicon nitride fibers produced from perhydropolysilazane[J]. J Ceram Soc Japan, 1990, 98(1133):104–107.
[24]张宗波,曾凡,罗永明,等.聚硅氮烷的应用研究进展[J].有机硅材料, 2013, 27(3):216–222.ZHANG Zongbo, ZENG Fan, LUO Yongming, et al. Silicone Mater,2013, 27(3):216–222.
[25] KOKOTT S, MOTZ G. Cross-linking via electron beam treatment of a tailored polysilazane(ABSE)for processing of ceramic SiCN-fibers[J].Soft Mater, 2007, 4(2/4):165–174.
[26] TRASSL S, KLEEBE H J, ST?RMER H, et al. Characterization of the free-carbon phase in Si—C—N ceramics:Part II, comparison of different polysilazane precursors[J]. J Am Ceram Soc, 2002, 85(5):1268–1274.
[27] KOKOTT S, MOTZ G. Modifizierung des ABSE-polycarbosilazans mit multi-walled carbon nanotubes zur herstellung spinnf?higer massen[J]. Materialwissenschaft Werkst, 2007, 38(11):894–900.
[28] KOKOTT S, HEYMANN L, MOTZ G. Rheology and processability of multi-walled carbon nanotubes—ABSE polycarbosilazane composites[J]. J Eur Ceram Soc, 2008, 28(5):1015–1021.
[29] FLORES O, BORDIA R K, BERNARD S, et al. Processing and characterization of large diameter ceramic SiCN monofilaments from commercial oligosilazanes[J]. RSC Adv, 2015, 5(129):107001–107011.
[30] FLORES O, SCHMALZ T, KRENKEL W, et al. Selective cross-linking of oligosilazanes to tailored meltable polysilazanes for the processing of ceramic SiCN fibres[J]. J Mater Chem A, 2013, 1(48):15406–15415.
[31] LU L, FENG C X, SONG Y C. Curing polysilazane fibres by exposure to boron trichloride[J]. J Mater Sci Lett, 1998, 17(6):481–484.
[32] LU L, SONG Y C, FENG C X. Composition and structure of boron-containing Si:N:C fibres at high temperature[J]. J Mater Sci Lett,1998, 17(7):599–602.
[33] YANG X J, LI B, LI D, et al. High-temperature properties and interface evolution of silicon nitride fiber reinforced silica matrix wave-transparent composite materials[J]. J Eur Ceram Soc, 2019,39(2/3):240–248.
[34] YANG X J, LI B, LI D, et al. Fabrication and oxidation resistance of silicon nitride fiber reinforced silica matrix wave-transparent composites[J]. J Mater Sci Technol, 2019, 35(12):2761–2766.
[35]罗小雨,李晓鸿,张梦娜,等.聚硅氮烷的干法纺丝及纤维的紫外辐照交联研究[J].硅酸盐通报, 2023, 42(6):2197–2205.LUO Xiaoyu, LI Xiaohong, ZHANG Mengna, et al. Bull Chin Ceram Soc, 2023, 42(6):2197–2205.
[36] WANG P, CHENG L F, ZHANG Y N, et al. Flexible SiC/Si3N4composite nanofibers with in situ embedded graphite for highly efficient electromagnetic wave absorption[J]. ACS Appl Mater Interfaces, 2017, 9(34):28844–28858.
[37] SEIFOLLAHI BAZARJANI M, KLEEBE H J, MüLLER M M, et al.Nanoporous Silicon Oxycarbonitride Ceramics Derived from Polysilazanes in situ Modified with Nickel Nanoparticles[J]. Chem Mater, 2011, 23(18):4112–4123.
[38]王丹,郭香,李鹏飞,等.全氢聚硅氮烷–氧化硅的转化过程研究[J].化学学报, 2022, 80(6):734–740.WANG Dan, GUO Xiang, LI Pengfei, et al. Acta Chim Sin, 2022,80(6):734–740.
[39]梁倩影,张宗波,黄文文,等.全氢聚硅氮烷衍生法制备耐高温抗氧化SiON涂层[J].涂料工业, 2017, 47(7):1–5.LIANG Qianying, ZHANG Zongbo, HUANG Wenwen, et al. Paint Coat Ind, 2017, 47(7):1–5.
[40] ZHAN Y, GROTTENMüLLER R, LI W, et al. Evaluation of mechanical properties and hydrophobicity of room-temperature,moisture-curable polysilazane coatings[J]. J Appl Polym Sci, 2021,138(21):e50469.
[41]向天意,李端,李俊生,等.高温电磁透波材料的研究进展[J].材料导报, 2023, 37(18):43–53.XIANG Tianyi, LI Duan, LI Junsheng, et al. Mater Rep, 2023, 37(18):43–53.
[42] KANDI K K, PUNUGUPATI G, PAGIDI M, et al. A novel gelcast SiO2–Si3N4–BN ceramic composites for radome applications[J].Silicon, 2022, 14(13):8179–8192.
[43]沈绥,卢振西,段玉婷,等.无碳氮化硼前驱体研究进展[J].辽宁化工, 2023, 52(11):1633–1638.SHEN Sui, LU Zhenxi, DUAN Yuting, et al. Liaoning Chem Ind, 2023,52(11):1633–1638.
[44] TOURY B, MIELE P, CORNU D, et al. Boron nitride fibers prepared from symmetric and asymmetric alkylaminoborazines[J]. Adv Funct Mater, 2002, 12(3):228.
[45] TAN J, GE M, YU S Q, et al. Microstructures and properties of ceramic fibers of h-BN containing amorphous Si3N4[J]. Materials,2019, 12(23):3812.
[46] DU Y A, WANG B, LI W, et al. Design and synthesis of a novel spinnable polyborazine precursor with high ceramic yield via one-pot copolymerization[J]. J Am Ceram Soc, 2021, 104(11):5509–5520.
[47] MENG F X, LI W, DU Y A, et al. Insight into the evolution process from novel polyborazine precursor PPMAB to inorganic BN fiber[J].Ceram Int, 2022, 48(22):33373–33380.
[48] DU Y A, WANG B, MENG F X, et al. Nearly stoichiometric BN fiber with high crystallinity achieved by boron trichloride assisted curing process[J]. J Am Ceram Soc, 2022, 105(1):82–89.
[49] ZHANG Y B, WANG B, MENG F X, et al. Influence of micro-tension on fiber orientation and crystallization in continuous polymer-derived boron nitride fiber[J]. Ceram Int, 2024, 50(2):3270–3275.
[50]杜贻昂,王兵,王应德.一种高陶瓷产率的无碳氮化硼先驱体及其合成方法[P]. CN113716581B. 2023–03–14.DU Y A, WANG B, WANG Y. Carbon-free boron nitride precursor with high ceramic yield and synthesis method thereof. CN113716581B.2023–03–14.
[51] DU Y A, WANG B, ZHANG Y B, et al. Online preparation of high-quality BN coatings with atomic diffusion based on carbon-free water-soluble precursor[J]. J Adv Ceram, 2024, 13(3):272–281.
[52]龙鑫. SiCN和SiBN纤维组成结构调控与性能研究[D].长沙:国防科技大学, 2020.LONG Xin. Study on the Composition, structure and Performance of SiCN and SiBN Fibers[D]. Changsha:National University of Defense Technology, 2020.
[53] RIEDEL R, KIENZLE A, DRESSLER W, et al. A silicoboron carbonitride ceramic stable to 2 000℃[J]. Nature, 1996, 382(6594):796–798.
[54] VIARD A, GOTTARDO L, LOPEZ-FERBER D, et al. Molecular design of melt-spinnable co-polymers as Si—B—C—N fiber precursors[J].Dalton Trans, 2017, 46(39):13510–13523.
[55] BALDUS P, JANSEN M, SPORN D. Ceramic fibers for matrix composites in high-temperature engine applications[J]. Science, 1999,285(5428):699–703.
[56] FUNAYAMA O, NAKAHARA H, TEZUKA A, et al. Development of Si—B—O—N fibres from polyborosilazane[J]. J Mater Sci, 1994, 29(8):2238–2244.
[57] DIRECT TO PHASE II–production of silicon boron nitride(SiBN)fibers for ceramic matric composite(CMC)radomes in hypersonic applications,[OL].[2023–03–08]. https://www.highergov.com/sbiropportunity/direct-to-phase-ii-production-of-silicn231-d06-sbir-2023-9a589098/
[58] ANDERSEN C A, KEIL K, MASON B. Silicon oxynitride:A meteoritic mineral[J]. Science, 1964, 146(3641):256–257.
[59] HUANG Z K, GREIL P, PETZOW G. Formation of silicon oxinitride from Si3N4 and SiO2 in the presence of Al2O3[J]. Ceram Int, 1984,10(1):14–17.
[60] BILLY M, BOCH P, DUMAZEAU C, et al. Preparation and properties of new silicon oxynitride based ceramics[J]. Ceram Int, 1981, 7(1):13–18.
[61] YU G E, PARRICK J, EDIRISINGHE M, et al. Synthesis of silicon oxynitride from a polymeric precursor[J]. J Mater Sci, 1993, 28(15):4250–4254.
[62]宋永才,李群力,冯春祥.聚硅氮烷的热分解特性研究[J].高分子学报, 1995(1):1–6.SONG Yongcai, LI Qunli, FENG Chunxiang. Acta Polym Sin, 1995(1):1–6.
[63]张俊宝,雷廷权,温广武,等.氮氧化硅合成研究进展[J].材料科学与工艺, 2001, 9(4):434–441.ZHANG Junbao, LEI Tingquan, WEN Guangwu, et al. Mater Sci Technol, 2001, 9(4):434–441.
[64] YU Y F, MAH T I. Si—O—N ceramics from organosilicon polymers[J].MRS Online Proc Libr, 1986, 73(1):559–564.
[65] GUNJI T, TANIGUCHI Y, ABE Y. Preparation of polysiloxazanes and their transformation to silicon oxynitride[J]. J Ceram Soc Japan,2006, 114(1330):492–496.
[66] IWASE Y, HORIE Y, DAIKO Y, et al. Synthesis of a novel polyethoxysilsesquiazane and thermal conversion into ternary silicon oxynitride ceramics with enhanced thermal stability[J]. Materials, 2017,10(12):1391.
[67] IWASE Y, HORIE Y, HONDA S, et al. Microporosity and CO2capture properties of amorphous silicon oxynitride derived from novel polyalkoxysilsesquiazanes[J]. Materials, 2018, 11(3):422.
[68] ZHANG Z B, WANG R, WANG X J, et al. Synthesis and thermal behavior of polymeric precursor for carbon-free silicon oxynitride ceramic[J]. J Appl Polym Sci, 2012, 123(2):1094–1099.
基本信息:
DOI：10.14062/j.issn.0454-5648.20240142
中图分类号:TQ174.1
引用信息:
[1]龙鑫,王驰原,邵长伟,等.先驱体转化氮化物高温透波陶瓷研究进展[J].硅酸盐学报,2024,52(09):2862-2874.DOI:10.14062/j.issn.0454-5648.20240142.
基金信息:
国家自然科学基金(52073304,52103364); 国防科技大学自主科研项目(ZK21-26,22-079); 湖南省自然科学基金(2022JJ 30045)
2024-02-23
2024
2024-08-09
2024
1
2024-09-02
2024-09-02
2024-09-02