超细活性水镁石是一种重要的环保型阻燃材料。使用2种硅烷偶联剂对水镁石超细粉进行了表面改性试验。将改性后的水镁石粉添加到聚丙烯(polypropylene,PP)中,研究了硅烷改性对PP/水镁石复合材料性能的影响。通过对改性前后粉体的扫描电镜(scanningelec tronmicroscope,SEM),Fourier变换红外光谱以及PP/水镁石复合材料新鲜断面的SEM分析等手段,研究硅烷偶联剂对水镁石粉改性的效果和改性机理。结果表明:偶联剂硅烷A174和硅烷FR693的最佳用量分别为水镁石粉质量的1.5%和1.0%,改性温度为80℃。改性可以使PP/水镁石复合材料的悬臂梁缺口冲击强度提高0.3kJ/m2,弯曲模量提高30%以上,并使材料的阻燃性能提高。使用偶联剂硅烷FR693可以使复合材料的拉伸强度提高1MPa,2种偶联剂都不能提高断裂伸长率及弯曲强度。
Abstract：Surface-modified ultra-fine brucite powder is a kind of environment-friendly fire-retardant of polymer. The ultra-fine brucite powder was surface-treated with two kinds of silane(A174 and FR693), and then filled into polypropylene (PP) as a kind of fire-retardant aimed. The effect of modification by silane on the properties of PP/brucite composite material was studied. The effect and modification mechanism were investigated by means of Fourier transfer infrared analysis, scanning electron microscopy of brucite powder and the fresh new surface of PP/brucite. The results show that the optimal dosage of brucite powde for silane A174 and silane FR693 is 1.5% and 1.0% in mass respectively and the temperature of surface treatment is 80 ℃. It indicates that the surface modification can enhance the izod impact strength of PP/Mg(OH)2 composite material by 0.3 kJ/m2, the bend modulus about 30%, and the retardant degree is enhanced to V0 from V1. The tensile strength of the composite material surface modified with silane FR693 can be increased 1 MPa. The bending strength and elongation at break of the material are not improved by both silane.
[1]WEBERM.Mineralflameretardants———overviewandfuture trends[J].IndMiner,2000(2):19—28.
[2]杜高翔,郑水林,李杨.阻燃用氢氧化镁及水镁石粉体的表面改性研究现状[J].非金属矿,2002,25(增刊):10—13.DUGaoxiang,ZHENGShuilin,LIYang.Non MetMiner(in Chinese),2002,25(suppl):10—13.
[3]陆开俊.水镁石应用研究现状[J].矿产保护与利用,1996(2):33—35.LUKaijun.JMinerProtectionUse(inChinese),1996(2):33—35.
[4]郭如新.水镁石及其在氢氧化镁阻燃剂生产中的应用[J].海盐湖与化工,1997,26(1):5—9.GUORuxin.SeaSaltLakeChemTechnol(inChinese),1997,26(1):5—9.
[5]倪忠斌,陈明清,杨成,等.低烟无卤阻燃电缆料的研制[J].无锡轻工大学学报,2001,20(5):500—502.NIZhongbin,CHENMingqing,YANGCheng,etal.JWuxi LightIndUniv(inChinese),2001,20(5):500—502.
[6]杜高翔.超细活性水镁石阻燃填料的制备研究[D].北京:北京工业大学,2002.11,34—40.DUGaoxiang.Thepreparationofsuper fineandsurfacemodi fiedbrucitepowderfillerusedasakindoffire retardant(in Chinese,dissertation).Beijing:BeijingUniversityofTechnol ogy,2002.11,34—40.
[7]冯嘉春,陈鸣才,张秀菊,等.稀土偶联剂(REC)对PP/Mg(OH)2体系性能的影响[J].中国塑料,2001,10:57—60.FENGJiachun,CHENMingcai,ZHANGXiuju,etal.Chin Plast(inChinese),2001,10:57—60.
基本信息:
中图分类号:TQ314.24
引用信息:
[1]杜高翔,郑水林,李杨.超细水镁石的硅烷偶联剂表面改性[J].硅酸盐学报,2005(05):659-664.
2005-05-26
2005-05-26