针对大体积混凝土绝热温升计算中粉煤灰与矿渣的火山灰反应放热问题,利用微量热仪法测试了不同掺量粉煤灰和矿渣对水泥水化热及放热速率的影响规律,分析了粉煤灰和矿渣水化3 d以前的火山灰反应放热行为,采用X射线衍射与差示扫描量热–热重法研究了粉煤灰与矿渣对水泥早期水化及其火山灰放热行为的影响机理。结果表明:粉煤灰与矿渣水化3d时火山灰反应热分别约为3～5J/g和15～16J/g。粉煤灰对水泥水化的阻碍作用在水化24h前最为明显,其火山灰效应主要发生于水化24h之后;矿渣对水泥水化有促进作用,自加水开始即表现出一定的火山灰效应。粉煤灰与矿渣掺入后有助于水泥水化产物中钙矾石的稳定,钙矾石抑制了水泥水化,Ca(OH)2生成量减少,因而粉煤灰与矿渣的火山灰反应也受到影响。
Abstract：In order to evaluate the pozzolanic reaction heat of fly ash(FA) and ground granulated blastfurnace slag(GGBS) in tem-perature simulation of mass concrete,the influence of replacement of FA and GGBS on the hydration process and heat rate of cement was investigated via microcalorimetry,and the behaviors of pozzolanic reaction heat of FA and GGBS before 3 d were analyzed.Re-action heat of FA and GGBS at early age was discussed by X-ray diffraction and differential scanning calorimetry–thermogravimetry(DSC–TG),respectively.The mechanism of pozzolanic.The results show that the pozzolanic reaction heat of FA and GGBS is 3–5 J/g and 15–16 J/g.The FA has a negative effect on the cement hydration before 24 h,but its pozzolanic effect plays a positive effect on the cement hydration after 24 h.The pozzolanic effect of the GGBS accelerates the cement hydration at early age.Ettringite is more steady in the cement hydration production when FA or GGBS is added,which delays the hydration of cement and produce of Ca(OH)2.Therefore,the pozzolanic reaction of the FA and GGBS can be affected.
[1]朱平华,彭述权,俞静.高层建筑基础大体积混凝土绝热温升计算[J].武汉理工大学学报,25(7):31–34.ZHU Pinghua,PENG Shuquan,YU Jing.J Wuhan Univ Technol(inChinese),25(7):31–34.
[2]陈华建,朱平华,夏古俊,等.基于绝热温升控制的GHPC配合比优化设计[J].武汉理工大学学报,2003,25(9):29–32.CHEN Huajian,ZHU Pinghua,XIA Gujun,et al.J Wuhan Univ Tech-nol(in Chinese),2003,25(9):29–32.
[3]汪冬冬,周士琼,大体积混凝土绝热温升试验研究[J].粉煤灰,2006(5):3–6.WANG Dongdong,ZHOU Shiqiong.Fly Ash(in Chinese),2006(5):3–6.
[4]代光富,黄明清,刘莲芝.溶解热法测定水泥水化热[J].水泥,2001(12):38–39.DAI Guangfu,HUANG Minqing,LIU Lianzhi.Cement(in Chinese),2001(12):38–39.
[5]施惠生,黄小亚.硅酸盐水泥水化热的研究及其进展[J].水泥,2009(12):4–10.SHI Huisheng,HUANG Xiaoya.Cement(in Chinese),2009(12):4–10.
[6]李虹燕,丁铸,邢锋,等.粉煤灰、矿渣对水泥水化热的影响[J].混凝土,2008(10):54–57.LI Hongyan,DING Zhu,XING Feng,et al.Concrete(in Chinese),2008(10):54–57.
[7]LANGAN B W,WENG K,WARD M A.Effect of silica fume and flyash on heat of hydration of Portland cement[J].Cem Conc Res,2002(32):1045–1051.
[8]DAVID J H,KURTE E.Heat of hydration of fly ash as a predictivetool[J].Fuel,1997,76(8):807–809.
[9]史非,王立久.高掺量粉煤灰矿渣水泥水化进程及水化热的研究[J].新型建筑材料,2003(1):14–16.SHI Fei,WANG Lijiu.New Building Mater(in Chinese),2003(1):14–16.
[10]WANG J C,YAN P Y.Influence of initial casting temperature anddosage of fly ash on hydration heat evolution of concrete under adia-batic condition[J].J Therm Anal Calorimetry,2006,85(3):755–760.
[11]LUCKMAN M,SATISH V,VENKATESWARAN D.Cementitious andpozzolanic behavior of electric arc furnace steel slags[J].Cem ConcrRes,2009(39):102–109.
[12]ZENG Q,LI KF,TEDDY FC,et al.Determination of cement hydrationand pozzolanic reaction extents for fly-ash cement pastes[J].ConstrucBuild Mater,2012(27):560–569.
[13]刘建生,沈燕华,张树青,等.宝钢高炉水淬矿渣自身水硬性和活性的关系[J].粉煤灰,2009(3):11–13.LIU Jiansheng,SHEN Yanhua,ZHANG Shuqing,et al.Fly Ash(inChinese),2009(3):11–13.
[14]YAMAMOTO T,KANAZU T,NAMBU M,et al.Pozzolanic reactivityof fly ash-API method and K-value[J].Fuel,2006(85):2345–2351.
[15]BENSTED J,BARNES P.Structure and performance of ce-ments(second edition)[M].USA:Taylor&Francis,2002.
基本信息:
DOI：10.14062/j.issn.0454-5648.2012.07.007
中图分类号:TU528
引用信息:
[1]王冲,杨长辉,钱觉时,等.粉煤灰与矿渣的早期火山灰反应放热行为及其机理[J].硅酸盐学报,2012,40(07):1050-1058.DOI:10.14062/j.issn.0454-5648.2012.07.007.
基金信息:
西部交通项目(2009318000033)资助
2012-07-15
2012-07-15