以硫铝酸盐水泥的主要矿物的硫铝酸钙(C4A3)为基础,用Sr2+对C4A3中的Ca2+进行取代,合成了新的水泥矿物——硫铝酸锶钙系列,研究了该系列矿物试样煅烧后的强度发展规律。结果表明:硫铝酸锶钙系列矿物试样经1300℃煅烧后的抗压强度明显高于硫铝酸钙,抗压强度最大的矿物组成为Ca1.50Sr2.50A3,其3d和28d抗压强度分别为76.6MPa和89.6MPa,用X射线衍射仪、扫描电子显微镜和差热分析仪等对熟料的形成和水化机理进行了初步分析,发现硫铝酸锶钙矿物水化产物主要是钙钒石(AFt),水化铝酸一钙(CAH10),Ca(OH)2以及Al2O3(aq)。
Abstract：A series of new cement minerals–Sr-bearing calcium sulphoaluminate were synthesized by substitution of Sr2+ for Ca2+ based on calcium sulphoaluminate(C4A3 S) which is the main mineral in sulphoaluminate cement.The compressive strength development of the system was also studied.The result shows that compressive strength of the samples burnt at 1300℃ is obviously higher than that of calcium sulphoaluminate.It was found that the optimum composition is Ca1.50Sr2.50A3 S.In addition,the formation and hydration mechanism of the clinkers were examined by means of X-ray diffraction,scanning electron microscope,differential thermal analysis,and so on.The main hydration product of Sr doped C4A3 S are ettringite(AFt),monocalcium aluminate hydrate(CAH10),Ca(OH)2 and Al2O3(aq).
[1]张丕兴,陈益民,史立萍,等.C4A3S晶体结构研究[J].中国建筑材料科学研究学报,1991,3(4):10–18.ZHANG Pixing,CHENG Yimin,SHI Liping,et al.J Chin Build Mater Acta(in Chinese),1991,3(4):10–18.
[2]王燕谋.硫铝酸盐水泥[M].北京:北京工业大学出版社,1999:36–41.WANG Yanmou.Sulphoalumninate Cement(in Chinese).Beijing:Beijing University of Technology Press,1999:36–41.
[3]TEOREANU I,MUNTEAN M,DRAGNEA I.Type3(CaO·Al2O3)-Mx(SO4)y compounds and compatibility relations in CaO·Al2O3-Mx(SO4)y systems[J].Cement,1986,83(1):39–46.
[4]YAN P.Investigation on the hydration of Sr-and Ba-bearing sulphoaluminate[C]//9th International Congress on the Chemistry of Cement,India,1992:411–417.
[5]程新.3CaO·3Al2O3·SrSO4的结构与特性和计算量子化学在一些水泥熟料矿物中的应用[D].武汉:武汉工业大学,1994.CHENG Xin.The structure and characteristic studies of3CaO·3Al2O3-SrSO4and the application of quantum chemistry on cement minerals(in Chinese,dissertation).Wuhan:Wuhan University of Technology,1994.
[6]程新,冯修吉.用量子化学方法计算3CaO·3Al2O3·SrSO4的水化活性[J].硅酸盐学报,1992,24(2):126–131.CHENG Xin,FENG Xiuji.J Chin Ceram Soc(in Chinese),1996,24(2):126–131.
[7]阎培喻.3CaO·3Al2O3·SrSO4浆体结构与强度的关系[J].武汉工业大学学报,1994,16(1):19–22.YAN Peiyu.J Wuhan Univ Technol(in Chinese),1994,16(1):19–22.
[8]徐国涛,杜鹤桂.硫铝酸锶钙水硬性矿物的合成与显微结构分析[J].东北大学学报,2000,21(1):70–72.XU Guotao,DU Hegui.J Northeastern Univ(in Chinese),2000,21(1):70–72.
[9]PUERTAS F,VARELA M T B,MOLINA S G.Kinetics of the thermal decomposition of C4A3S in air[J].Cem Concr Res,1995,25(3):572–580.
[10]龙世宗,廖广林,赵三银.含钡硫铝酸钙矿物烧成若干问题的研究[J].中国建材科技,1996,5(3):11–16.LONG Shizong,LIAO Guanglin,ZHAO Sanyin.Chin Build Mater Sci Tech(in Chinese),1996,5(3):11–16.
[11]常钧,芦令超,刘富田.含钡硫铝酸钙水泥矿物的研究[J].硅酸盐学报,1999,26(7):643–650.CHANG Jun,LU Lingchao,LIU Futian,et al.J Chin Ceram Soc(in Chinese),1999,26(7):643–650.
[12]杨南如.无机非金属材料图谱手册[M].武汉:武汉工业大学出版社,2000:254–263.YANG Nanru.The Handbook of Inorganic Matalloid Materials Atlas(in Chinese).Wuhan:Wuhan University of Technology Press,2000:254–263.
基本信息:
DOI：10.14062/j.issn.0454-5648.2010.04.030
中图分类号:TQ172.1
引用信息:
[1]常钧,谭文杰,黄睿,等.硫铝酸锶钙矿物的研究[J].硅酸盐学报,2010,38(04):666-670.DOI:10.14062/j.issn.0454-5648.2010.04.030.
基金信息:
国家“973”计划(2009CB21301);; 山东省自然科学基金(Y2008F49)资助项目
2010-04-15
2010-04-15