2025, 09, v.53 2651-2663
空心球状高熵钙钛矿氧化物的制备及其超级电容和电催化析氧性能(英文)
基金项目(Foundation): 国家自然科学基金(52472064)
邮箱(Email): suxinghua@chd.edu.cn;
DOI: 10.14062/j.issn.0454-5648.20240770
摘要:

采用微波溶剂热和煅烧处理相结合的方法制备了空心球状的高熵钙钛矿La(Cr0.2Mn0.2Fe0.2Ni0.2Cu0.2)O3粉体(HSHEPs),并研究了其超级电容和电催化析氧(OER)性能。结果表明,HS-HEPs在1 A/g的电流密度下具有406F/g的比电容,经过5000次充放电循环后,电容保持率为65%;HS-HEPs//AC(活性炭)非对称超级电容器在746W/kg的功率密度下,能量密度可达39.4 W·h/kg。此外,HS-HEPs在碱性电解液(1 mol/L KOH溶液)中,表现出较好的OER性能,在10 mA/cm2电流密度下的过电位为347 mV,Tafel斜率为54.13 mV/dec,并具有良好的电化学稳定性。本研究提供了一种制备空心球状高熵氧化物的方法,并为设计和开发具有优异超级电容及OER性能的材料提供了思路。

Abstract:

Introduction High-entropy oxides(HEOs) have attracted much attention in the field of electrochemistry due to their distinctive structural characteristics and unique properties. The multiple-principal elements in HEOs offer the multiple redox pairs and multiple possible active sites, which can enhance the energy storage capacity and the electrocatalytic performance. Although the notable progress is achieved in the development of HEOs electrodes, their electrochemical properties should be further improved to meet the requirements of high-performance supercapacitors and OER electrocatalysts. The abundant active sites for the Faradic redox reactions and short pathways for charge transportation could be constructed through the design of novel HEOs with advanced microstructures, thus improving the electrochemical properties. As advanced microstructures, a hollow structure has a great promise for energy storage and conversion because it can provide more accessible storage sites, more catalytic centers and a larger electrode/electrolyte contact area. It is thus expected that the construction of hollow structure is an alternative route to significantly promote the electrochemical properties of HEOs electrode materials. However, it is difficult to prepare the HEOs with a hollow structure due to the complexity of the high-entropy system. In this work, a hollow spherical high-entropy perovskite oxide of La(Cr0.2Mn0.2Fe0.2Ni0.2Cu0.2)O3(HS-HEPs) was prepared by microwave solvothermal process and subsequent calcination treatment. The as-prepared HS-HEPs exhibited the excellent electrochemical performance when used as an electrode material for supercapacitors and OER electrocatalysts due to the advantages resulted from the combination of high-entropy perovskite and special hollow structure. Methods HS-HEPs were prepared by microwave solvothermal process and subsequent calcination treatment. Typically, 0.134 mmol Cr(NO3)3·6H2O, 0.134 mmol Mn(NO3)2·4H2O, 0.134 mmol Fe(NO3)3·9H2O, 0.134 mmol Ni(NO3)2·6H2O, 0.134 mmol Cu(NO3)2·3H2O, and 0.5 mmol La(NO3)3·6H2O were dissolved in 30 mL ethanol under stirring for 1 h to obtain the homogeneous solution. Afterwards, 60 mg of carbon spheres were added in the solution under ultrasonic treatment for 30 min. The resulting mixture was transferred to a 50 mL microwave digestion vessel. The vessel was heated in a microwave oven at a power of 210 W for 10 min. Subsequently, the obtained mixture was centrifuged, washed with deionized water, and dried in a vacuum drying oven at 70 ℃ for 12 h. Finally, the obtained precursor powder was calcinated in a tube furnace with a heating rate of 3 ℃/min at 650 ℃ for 2 h to acquire HS-HEPs. The crystalline structure of the sample was determined by X-ray diffraction(XRD, D8 Davinci, Bruker Co., Germany). The morphology and microstructure of sample were characterized by field-emission scanning electron microscopy(FESEM, S-4800, Hitachi Co. Ltd., Japan) equipped with energy dispersive X-ray spectroscopy(EDS) and transmission electron microscopy(TEM, 2100F, JEOL Co., Japan). The X-ray photoelectron spectra were obtained by a X-ray photoelectron spectrometry(XPS, ESCALab 250, Thermo VG Co., USA). The supercapacitor and OER performance of the sample were measured on a CHI 660E electrochemical workstation(Shanghai Chenhua Instrument Co., China). Results and discussion The as-prepared samples display a cubic perovskite crystalline structure and a hollow sphere morphology. According to the XPS analysis, the variable oxidation states of Cr, Fe and Mn present in the HS-HEPs, which benefits the Faradaic redox reactions and increases the capacitance. In addition, the existence of high concentration of oxygen vacancies in HS-HEPs is beneficial to enhancing the capacitance and OER activity. Based on the GCD curve, the specific capacitance of HS-HEPs is estimated to be 406 F/g at 1 A/g. After GCD cycles of 5000 at a current density of 5 A/g, 65% capacitance is retained, implying a good long-term electrochemical stability. An asymmetric supercapacitor device(HS-HEPs//AC) with a two electrode configuration is assembled. A maximum energy density of 39.4 W·h/kg is achieved at power density of 746 W/kg. The OER activity of HS-HEPs is evaluated by a linear sweep voltammetry(LSV) polarization curve in 1 mol/L KOH aqueous solution using a standard three-electrode system. The overpotential of HS-HEPs is identified as 347 mV versus RHE for achieving a current density of 10 mA/cm2, which is smaller than that of commercial IrO2(372 mV). The HS-HEPs possess the excellent electrochemical performance, which can be ascribed to the high specific surface area, abundant active sites, and high oxygen vacancy content, resulting from the combination of high-entropy perovskite and special hollow structure. Conclusions High-entropy La(Cr0.2Mn0.2Fe0.2Ni0.2Cu0.2)O3 hollow spheres with a perovskite crystalline structure were prepared by microwave solvothermal process and subsequent calcination treatment. The HS-HEPs possessed the excellent electrochemical performance, which could be ascribed to the high specific surface area, abundant active sites, and high oxygen vacancy content, resulting from the combination of high-entropy perovskite and special hollow structure. Based on the electrochemical performance, HS-HEPs could be used as supercapacitor electrode material and OER electrocatalysts. This work could provide a strategy to design and prepare high-entropy oxides with a hollow sphere structure, having promising applications in energy storage and conversion.

参考文献

[1]TAO H C,FAN Q,MA T,et al.Two-dimensional materials for energy conversion and storage[J].Prog Mater Sci,2020,111:100637.

[2]ZHANG F F,GAO M Q,HUANG S Q,et al.Redox targeting of energy materials for energy storage and conversion[J].Adv Mater,2022,34(25):e2104562.

[3]WEN Q B,QU F M,YU Z J,et al.Si-based polymer-derived ceramics for energy conversion and storage[J].J Adv Ceram,2022,11(2):197-246.

[4]ZHAO J Y,BURKE A F.Review on supercapacitors:Technologies and performance evaluation[J].J Energy Chem,2021,59:276-291.

[5]GREENHALGH E S,NGUYEN S,VALKOVA M,et al.A critical review of structural supercapacitors and outlook on future research challenges[J].Compos Sci Technol,2023,235:109968.

[6]HUANG J,XIE Y P,YOU Y,et al.Rational design of electrode materials for advanced supercapacitors:From lab research to commercialization[J].Adv Funct Mater,2023,33(14):2213095.

[7]ZHANG Y,JING X,YAN X H,et al.Rational design of Ni Mn-based electrode materials for high-performance supercapacitors[J].Coord Chem Rev,2024,499:215494.

[8]WANG Y L,AI Y L,YANG S W,et al.Facile synthesis and supercapacitor performance of M3O4(M=Fe Co Cr Mn Mg) high entropy oxide powders[J].J Inorg Mater,2021,36(4):425.

[9]YANG W Y,WANG J,GAO S,et al.Photo-assisted charging of carbon fiber paper-supported Ce O2/Mn O2 heterojunction and its long-lasting capacitance enhancement in dark[J].J Adv Ceram,2022,11(11):1735-1750.

[10]SUN H N,XU X M,KIM H,et al.Advanced electrocatalysts with unusual active sites for electrochemical water splitting[J].Info Mat,2024,6(1):e12494.

[11]QIU P,LI C,LIU B,et al.Materials of solid oxide electrolysis cells for H2O and CO2 electrolysis:A review[J].J Adv Ceram,2023,12(8):1463-1510.

[12]SUN H N,XU X M,KIM H,et al.Electrochemical water splitting:Bridging the gaps between fundamental research and industrial applications[J].Energy Environ Mater,2023,6(5):e12441.

[13]SAI KUMAR A,SIDDIQUI Q T,PABBA D P,et al.Enhancing efficiency of photoelectrochemical water splitting using zinc vanadate nanosheets (ZV) on manganese vanadate needle flowers (MV)supported by carbon nanofibers[J].Ceram Int,2024,50(19):35975-35984.

[14]VOJDANI SAGHIR A,MOLLAZADEH BEIDOKHTI S,VAHDATIKHAKI J.A comparative study on the electrocatalytic OER activity of mesoporous high-entropy oxide and medium-entropy oxide nanoparticles through SCS method[J].Ceram Int,2024,50(13):24070-24087.

[15]JAMESH M I,HARB M.Tuning the electronic structure of the earth-abundant electrocatalysts for oxygen evolution reaction (OER) to achieve efficient alkaline water splitting-A review[J].J Energy Chem,2021,56:299-342.

[16]DHANDAPANI E,THANGARASU S,RAMESH S,et al.Recent development and prospective of carbonaceous material,conducting polymer and their composite electrode materials for supercapacitor:Areview[J].J Energy Storage,2022,52:104937.

[17]WU B,MENG H B,MORALES D M,et al.Nitrogen-rich carbonaceous materials for advanced oxygen electrocatalysis:Synthesis,characterization,and activity of nitrogen sites[J].Adv Funct Mater,2022,32(31):2204137.

[18]WANG H X,ZHANG K H L,HOFMANN J P,et al.The electronic structure of transition metal oxides for oxygen evolution reaction[J].JMater Chem A,2021,9(35):19465-19488.

[19]DU X M,REN X L,XU C J,et al.Recent advances on the manganese cobalt oxides as electrode materials for supercapacitor applications:Acomprehensive review[J].J Energy Storage,2023,68:107672.

[20]ZHANG J Y,LIAN J S,JIANG Q,et al.Boosting the OER/ORR/HERactivity of Ru-doped Ni/Co oxides heterostructure[J].Chem Eng J,2022,439:135634.

[21]GAO X R,WANG P K,PAN Z H,et al.Recent progress in two-dimensional layered double hydroxides and their derivatives for supercapacitors[J].Chem Sus Chem,2020,13(6):1226-1254.

[22]TOMBOC G M,KIM J,WANG Y T,et al.Hybrid layered double hydroxides as multifunctional nanomaterials for overall water splitting and supercapacitor applications[J].J Mater Chem A,2021,9(8):4528-4557.

[23]CHEN D Z,FAN Q Q,ZHOU J,et al.Toward understanding the formation mechanism and OER catalytic mechanism of hydroxides by in situ and operando techniques[J].Angew Chem Int Ed,2023,62(51):e202309293.

[24]HU Y,ZHENG Y,JIN J,et al.Understanding the sulphur-oxygen exchange process of metal sulphides prior to oxygen evolution reaction[J].Nat Commun,2023,14(1):1949.

[25]MELKIYUR I,RATHINAM Y,KUMAR P S,et al.A comprehensive review on novel quaternary metal oxide and sulphide electrode materials for supercapacitor:Origin,fundamentals,present perspectives and future aspects[J].Renew Sustain Energy Rev,2023,173:113106.

[26]RAM KUMAR K,MAIYALAGAN T.Iron nickel sulphide embedded on multi-walled carbon nanotubes as efficient electrocatalysts for oxygen evolution reaction in alkaline medium[J].Ceram Int,2023,49(1):1195-1202.

[27]ADALATI R,SHARMA M,SHARMA S,et al.Metal nitrides as efficient electrode material for supercapacitors:A review[J].J Energy Storage,2022,56:105912.

[28]WEI B B,MING F W,LIANG H F,et al.All nitride asymmetric supercapacitors of niobium titanium nitride-vanadium nitride[J].JPower Sources,2021,481:228842.

[29]YANG Z G,XU H M,SHUAI T Y,et al.Recent progress in the synthesis of transition metal nitride catalysts and their applications in electrocatalysis[J].Nanoscale,2023,15(28):11777-11800.

[30]ZONG Q,LIU C F,YANG H,et al.Tailoring nanostructured transition metal phosphides for high-performance hybrid supercapacitors[J].Nano Today,2021,38:101201.

[31]KANDEL M R,PAN U N,PAUDEL D R,et al.Hybridized bimetallic phosphides of Ni-Mo,Co-Mo,and Co-Ni in a single ultrathin-3D-nanosheets for efficient HER and OER in alkaline media[J].Compos Part B Eng,2022,239:109992.

[32]ZEENAT,AHMAD Z,MAQBOOL A,et al.One-pot solvothermal synthesis of highly catalytic Janus transition metal phosphides (TMPs)for high performance OER[J].Fuel,2023,331:125913.

[33]CHEN Y C,YANG H C,HAN Z J,et al.MXene-based electrodes for supercapacitor energy storage[J].Energy Fuels,2022,36(5):2390-2406.

[34]WEI B,FU Z H,LEGUT D,et al.Rational design of highly stable and active MXene-based bifunctional ORR/OER double-atom catalysts[J].Adv Mater,2021,33(40):e2102595.

[35]WANG Z,XU J,YANG J H,et al.Ultraviolet/ozone treatment for boosting OER activity of MOF nanoneedle arrays[J].Chem Eng J,2022,427:131498.

[36]SAHOO R,GHOSH S,CHAND S,et al.Highly scalable and p H stable2D Ni-MOF-based composites for high performance supercapacitor[J].Compos Part B Eng,2022,245:110174.

[37]ZENG X J,YE Y F,WANG Y Q,et al.Honeycomb-like MXene/Ni Fe Px-NC with“continuous”single-crystal enabling high activity and robust durability in electrocatalytic oxygen evolution reactions[J].J Adv Ceram,2023,12(3):553-564.

[38]YANG B,LüG X,MA J T.Electrocatalytic water splitting over nickel iron hydroxide-cobalt phosphide composite electrode[J].J Inorg Mater,2024,39(4):374.

[39]JOSHI B,SAMUEL E,HUH J,et al.Hierarchically decorated Zn O/Co Ox nanoparticles on carbon fabric for high energy-density and flexible supercapacitors[J].Ceram Int,2024,50(21):43324-43333.

[40]KHAN A,JAVED F,ALAHMARI S D,et al.Dysprosium oxide nanoparticle decorated on reduced graphene oxide sheets:Active and sustainable electrocatalyst for OER[J].Ceram Int,2024,50(17):30188-30198.

[41]JIAO Y T,DAI J,FAN Z H,et al.Overview of high-entropy oxide ceramics[J].Mater Today,2024,77:92-117.

[42]GUO M,LIU Y F,ZHANG F N,et al.Inactive Al3+-doped La(Co Cr Fe Mn Ni Alx)1/(5+x)O3 high-entropy perovskite oxides as high performance supercapacitor electrodes[J].J Adv Ceram,2022,11(5):742-753.

[43]LI L L,JI P C,GENG C,et al.Facile synthesis of high-entropy(Co0.2Cr0.2Fe0.2Mn0.2Ni0.2)3O4 nanopowders and their electrochemical properties as supercapacitor electrode[J].J Energy Storage,2023,73:109182.

[44]NGUYEN T X,LIAO Y C,LIN C C,et al.Advanced high entropy perovskite oxide electrocatalyst for oxygen evolution reaction[J].Adv Funct Mater,2021,31(27):2101632.

[45]KANTE M V,WEBER M L,NI S,et al.A high-entropy oxide as high-activity electrocatalyst for water oxidation[J].ACS Nano,2023,17(6):5329-5339.

[46]HAN C X,XU X Q,MU H,et al.Construction of hierarchical sea urchin-like manganese substituted nickel cobaltite@tricobalt tetraoxide core-shell microspheres on nickel foam as binder-free electrodes for high performance supercapacitors[J].J Colloid Interface Sci,2021,596:89-99.

[47]WANG D,WANG Y J,FU Z Y,et al.Cobalt-nickel phosphate composites for the all-phosphate asymmetric supercapacitor and oxygen evolution reaction[J].ACS Appl Mater Interfaces,2021,13(29):34507-34517.

[48]SUN Y H,TANG T M,XIAO L Y,et al.Nanoflower-like high-entropy co-Fe-Cr-Mo-Mn spinel for oxygen evolution[J].Chemistry,2024,30(17):e202303779.

[49]HE H,KOU P Z,ZHANG Z G,et al.Coupling high entropy oxide with hollow carbon spheres by rapid microwave solvothermal strategy for boosting oxygen evolution reaction[J].J Colloid Interface Sci,2024,653(Pt A):179-188.

[50]NAN H S,LV S H,XU Z J,et al.Inducing the cocktail effect in yolk-shell high-entropy perovskite oxides using an electronic structural design for improved electrochemical applications[J].Chem Eng J,2023,452:139501.

[51]LAI D W,LING L,SU M F,et al.From amorphous to crystalline:Auniversal strategy for structure regulation of high-entropy transition metal oxides[J].Chem Sci,2023,14(7):1787-1796.

[52]MENG Z S,GONG X L,XU J,et al.A general strategy for preparing hollow spherical multilayer structures of oxygen-rich vacancy transition metal oxides,especially high entropy perovskite oxides[J].Chem Eng J,2023,457:141242.

[53]WANG J Y,CUI Y,WANG D.Design of hollow nanostructures for energy storage,conversion and production[J].Adv Mater,2019,31(38):e1801993.

[54]WANG J Y,WAN J W,WANG D.Hollow multishelled structures for promising applications:Understanding the structure-performance correlation[J].Acc Chem Res,2019,52(8):2169-2178.

[55]LI Q L,SUN F M,ZHANG D,et al.Recent progress of hollow structure platform in assisting oxygen evolution reaction[J].Chem Eng J,2023,452:139232.

[56]JIA Y G,CHEN S J,SHAO X,et al.Synergetic effect of lattice distortion and oxygen vacancies on high-rate lithium-ion storage in high-entropy perovskite oxides[J].J Adv Ceram,2023,12(6):1214-1227.

[57]JI X Q,YANG F,DU Y Z,et al.Highly active and durable La0.6Ca0.4(Cr Mn Fe Co2Ni)O3 high entropy perovskite oxide as electrocatalyst for oxygen evolution reaction in alkaline media[J].JMater Sci Technol,2024,168:71-78.

[58]GOVINDARAJAN D,ETESAMI M,NOOTONG K,et al.Nano-tablets and rods-shaped Fe and Ni oxide/hydroxide encapsulated graphene for asymmetric supercapacitor and OER applications[J].JEnergy Storage,2023,74:109435.

[59]LINDSTR?M H,S?DERGREN S,SOLBRAND A,et al.Li+ion insertion in Ti O2 (anatase).2.voltammetry on nanoporous films[J].JPhys Chem B,1997,101(39):7717-7722.

[60]WANG S,YUAN Z S,ZHANG X,et al.Non-metal ion co-insertion chemistry in aqueous Zn/Mn O2 batteries[J].Angew Chem Int Ed,2021,60(13):7056-7060.

[61]CAO Y,LIANG J,LI X,et al.Recent advances in perovskite oxides as electrode materials for supercapacitors[J].Chem Commun,2021,57(19):2343-2355.

[62]JIN T,SANG X H,UNOCIC R R,et al.Mechanochemical-assisted synthesis of high-entropy metal nitride via a soft urea strategy[J].Adv Mater,2018,30(23):e1707512.

[63]CHAI S S,ZHANG L,ZHANG W B,et al.Acid etching halloysite loaded cobalt boride material for supercapacitor electrode application[J].Appl Clay Sci,2022,218:106426.

[64]SURE D J,SRI MAHA VISHNU D D,KIM D H,et al.Facile electrochemical synthesis of nanoscale (Ti Nb Ta Zr Hf)C high-entropy carbide powder[J].Angew Chem Int Ed,2020,59(29):11830-11835.

[65]RONG W,CHEN Y F,DANG R,et al.Amorphous high-entropy Ir Ru Cr Fe Co Ni Ox as efficient water splitting oxygen evolution reaction electrocatalysts[J].J Alloys Compd,2024,971:172786.

[66]SCHWEIDLER S,TANG Y S,LIN L,et al.Synthesis of perovskite-type high-entropy oxides as potential candidates for oxygen evolution[J].Front Energy Res,2022,10:983979.

基本信息:

DOI:10.14062/j.issn.0454-5648.20240770

中图分类号:TM53;TQ426

引用信息:

[1]张帅,娄程广,李汶金等.空心球状高熵钙钛矿氧化物的制备及其超级电容和电催化析氧性能(英文)[J].硅酸盐学报,2025,53(09):2651-2663.DOI:10.14062/j.issn.0454-5648.20240770.

基金信息:

国家自然科学基金(52472064)

检 索 高级检索

引用

GB/T 7714-2015 格式引文
MLA格式引文
APA格式引文