以硝酸铋、碘化钾为原料,采用沉淀法制备出花状的碘化氧铋。用X射线衍射、扫描电子显微镜、紫外-可见漫反射吸收光谱和比表面孔径分析仪对样品进行了表征,研究了陈化时间对花状碘化氧铋的形成和光催化活性的影响,并对光催化反应机理进行了研究。结果表明:陈化时间为1 h的样品由纳米片紧密地交错在一起形成的花状结构组成,且直径最小;随着陈化时间的延长,样品的光催化活性先上升后下降,陈化时间为1 h的样品光催化活性最高。花状碘化氧铋对甲基橙的降解主要是通过空穴直接氧化途径进行。
Abstract：The flower-like BiOI was prepared via a facile precipitation route with Bi(NO3)3·5H2O and KI as raw materials at room temperature. The obtained samples were characterized by powder X-ray diffraction, scanning electron microscopy, UV–Vis diffuse reflectance and specific surface area analysis, respectively. The effect of aging time on the photocatalytic activity and the formation of the flower-like Bi OI were investigated, and the photocatalytic reaction mechanism was discussed. The results show that the sheet structure closely intertwines to form a flower-like structure in a small diameter when the aging time is 1 h. The methyl orange(MO) degradation rate firstly increases and then decreases with increasing the age time. The maximum rate of MO degradation is obtained when the catalyst is aged for 1 h. The photocatalytic degradation of MO on flower-like BiOI occurs due to the direct oxidation in the holes.
[1]KIJIMA N,MATANO K,SAITO M,et al.Oxidative catalytic cracking of n-Butane to lower alkenes over layered Bi OCl catalyst[J].Appl Catal A,2001,206(2):237–244.
[2]DELLINGER T M,BRAUN P V.Bi OCl nanoparticles synthesized in lyotropic liquid crystal nanoreactors[J].Scr Mater,2001,44(8/9):1893–1987.
[3]QIN X Y,CHENG H F,WANG W J,et al.Three dimensional Bi OX(X=Cl,Br and I)hierarchical architectures facile ionic liquid-assisted solvothermal synthesis and photocatalysis towards organic dye degradation[J].Mater Lett,2013,100:285–288.
[4]AI L H,ZENG Y,JIANG J.Hierarchical porous Bi OI architectures:Facile microwave nonaqueous synthesis,characterization and application in the removal of Congo red from aqueous solution[J].Chem Eng J,2014,235:331–339.
[5]SHI X J,CHEN X L,CHEN X,et al.Solvothermal synthesis of Bi OI hierarchical spheres with homogeneous sizes and their high photocatalytic performance[J].Mater Lett,2012,68:296–299.
[6]LI Y Y,WANG J S,YAO H C,et al.Efficient decomposition of organic compounds and reaction mechanism with Bi OI photocatalyst under visible light irradiation[J].J Mol Catal A:Chem,2011,334(1/2):116–122.
[7]汪冬梅,吴玉程,吕珺,等.Fe3+/Zn2+复合掺杂纳米Ti O2的结构及光催化性能[J].硅酸盐学报.2008,36(11):1526–1541.WANG Dongmei,WU Yucheng,LV Jun,et al.J Chin Ceram Soc,2008,36(11):1526–1541.
[8]龚潇,陈天虎,庆承松,等.Ti O2/α-Fe2O3复合光催化剂的制备及表征[J].硅酸盐学报.2008,36(6):838–843.GONG Xiao,CHEN Tianhu,QING Chengsong,et al.J Chin Ceram Soc,2008,36(6):838–843.
[9]DONG X L,DING W,ZHANG X F,et al.Mechanism and kinetics model of degradation of synthetic dyes by UV-vis/H2O2/freeioxallate complexes[J].Dye Pigments,2007,74(2):470–476.
[10]JIANG D L,CHEN L L,ZHU J J,et al.Novel p–n heterojunction photocatalyst constructed by porous graphite-like C3N4 and nanostructured Bi OI:facile synthesis and enhanced photocatalytic activity[J].Dalton Trans,2013,42(44):15726–15734.
[11]REDDY K,MARTHA S,PARIDA K.Fabrication of novel pBi OI/n-Zn Ti O3 heterojunction for degradation of rhodamine 6G under visible light irradiation[J].Inorg Chem,2013,52(11):6390-6401.
[12]CAO J,XU B Y,LIN H L,et al.Novel heterostructured Bi2S3/Bi OI photocatalyst:facile preparation,characterization and visible light photocatalytic performance[J].Dalton Trans,2012,41(37):11482–11490.
[13]SING K S W,EVERETT D H,HAUL R A W,et al.Reporting physisorption data for gas/solid systems[J].Pure Appl Chem,1982,54(11):2201–2218.
[14]DONG F,SUN Y J,FU M,et al.Room temperature synthesis and highly enhanced visible light photocatalytic activity of porous Bi OI/Bi OCl composites nanoplates microflowers[J].J Hazard Mater,2012,219:26–34.
[15]XU H,YAN J,XU Y G,et al.Novel visible-light-driven Ag X/graphite-like C3N4(X=Br,I)hybrid materials with synergistic photocatalytic activity[J].Appl Catal B,2013,129:182–193.
基本信息:
DOI：10.14062/j.issn.0454-5648.2015.01.17
中图分类号:TQ135.32;O643.36
引用信息:
[1]符烈,代黎明,卢临杭,等.花状碘化氧铋的简单制备与光催化性能[J],2015,43(01):103-108.DOI:10.14062/j.issn.0454-5648.2015.01.17.
基金信息:
江苏大学高级人才基金(12JDG106)项目