氧化铝陶瓷连续纤维具有耐高温、高强度、高模量、热导率低、绝缘性好、耐化学腐蚀能力强等特点，在航空航天、先进制造等领域具有重要的应用。本文对氧化铝基陶瓷连续纤维的制备、性能及应用进行了全面的综述，并对氧化铝基陶瓷连续纤维未来的发展方向进行了总结和展望，期望为未来氧化铝基陶瓷连续纤维的研制与应用提供参考。
Abstract：Alumina ceramic continuous fiber is one of the most important materials because of its high strength and modulus,high temperature resistance,chemical inertness in both oxidizing and reducing atmospheres even at high temperature,resistance to attack from non-oxide materials,good electrical insulation and low thermal conductivity.The high strength and high-temperature resistance have allowed the development of metal and ceramic matrix composites with high tensile strength or high-temperature load-bearing capability.Thus,alumina ceramic continuous fiber is of great importance in aerospace,advanced manufacturing,and other fields.The Al_2O3 content in alumina ceramic fiber is usually more than 70%(mass fraction),and generally contains a small amount of other oxides,such as SiO2,B_2O3,Fe_2O3,ZrO2,and etc.Amorphous SiO2,transition phase alumina,α-Al_2O3 and mullite are the common phases in alumina ceramic fibers,resulting in various phase compositions and microstructures.Chemical composition and the microstructure have great effects on the fibers’mechanical performance and temperature resistance.Depending on the chemical composition and the microstructure,the alumina ceramic fibers show the tensile strength from 1.5 GPa to 3.1 GPa,and a long-term using temperature varied from 1 000℃to 1 300℃.The careful selection is necessary according to the unique circumstances and conditions involved in the use and processing of the alumina fibers.Furthermore,the preparation of alumina ceramic fibers with controlled composition and microstructure is critical.Main methods for manufacturing alumina ceramic fibers can be classified as slurry process,melt-spinning process,prepolymerization process and sol-gel spinning process.The melt spinning method was limited in the length of the fibers,thus,it was not suitable for the preparation of the alumina continuous fibers.While it is difficult to prepare alumina fibers with high strength from the slurry method.Excellent alumina continuous fibers can be obtained through the pre-polymerization process and sol-gel spinning process,in which the sol-gel method shows the advantages of adjustable composition,uniform composition at the atomic level,relative moderate preparation conditions and low cost,becoming the most important preparation method for alumina ceramic continuous fibers.In the past decades,a family of alumina fibers have been developed,typically as the commercial 3M NextelTM alumina ceramic fibers,which have been used in a variety of areas.However,its export to China is restricted by developed countries because of the application in military field,such as aerospace.To develop the local production,many researchers of China have devoted to the preparation of alumina continuous ceramic fibers,mainly by new sol,that is,how to transform from the gel fiber to ceramic fiber.Fortunately,significant progress has been made recently,so that commercialization of the ceramic fiber comes to be true.This further promotes the applications of alumina ceramic fibers.However,there is still a certain gap in performance between the local produced fibers and the fibers abroad.Continued technological innovation is still an important task in the future.Summary and prospects At present,the development of alumina based ceramic continuous fiber in China is mainly carried out under the national academic financial support.The main work at current stage mainly focuses on how to produce the fibers which could meet the basic properties.Most research and development usually rely on model products.Few attention is paid to the research on relevant scientific mechanism and theory,resulting in lack of theoretical support for new applications and in lack of independent innovation ability.Since most of the applications of alumina continuous fiber are based on its performance of high temperature resistance and high strength,it can be predicted that improving the tensile strength and thermal resistance of alumina continuous fiber is still the main goal in the future.Therefore,it is believed as important work to carry out key basic theoretical research,to clarify the intrinsic relationship between the composition-structure-processing-performance of alumina ceramic fibers,and to establish a theoretical model of high-performance alumina ceramic continuous fiber.These investigations can direct the design and preparation of the fibers,to achieve breakthroughs hopefully in the strength and temperature resistance of alumina ceramic continuous fiber,and to furtherly promote the application of fiber and the composite in aerospace and the related fields.
[1] MATEEN T, FAISAL H, AFZAAL A. Overview of NextelTM based structures for space applications[J]. J Space Technol Sci, 2011, 1(1):88–94.
[2] COX B N, ZOK F W. Advances in ceramic composites reinforced by continuous fibers[J]. Curr Opin Solid State Mater Sci, 1996, 1(5):666–673.
[3] BANSAL N P. Handbook of Ceramic Composites[M]. Boston, MA:Springer US, 2005.
[4] KRENKEL W. Ceramic matrix composites:fiber reinforced ceramics and their applications[M]. Weinheim:Wiley-VCH, 2008.
[5] MICHALSKE T A, HELLMANN J R. Strength and toughness of continuous-alumina-fiber-reinforced glass-matrix composites[J]. J Am Ceram Soc, 1988, 71(9):725–731.
[6] KAYA C, GU X, AL-DAWERY I, et al. Microstructural development of woven mullite fibre-reinforced mullite ceramic matrix composites by infiltration processing[J]. Sci Technol Adv Mater, 2002, 3(1):35–44.
[7] RADSICK T, SARUHAN B, SCHNEIDER H. Damage tolerant oxide/oxide fiber laminate composites[J]. J Eur Ceram Soc, 2000,20(5):545–550.
[8] ALLAN R H, MICHAEL F G. High temperature properties of three Nextel ceramic fibers[C]//32nd International SAMPE Symposium,California, USA, 1987, 4:6–9.
[9] CHAWLA N, KERR M, CHAWLA K K. Monotonic and cyclic fatigue behavior of high-performance ceramic fibers[J]. J Am Ceram Soc,2005, 88(1):101–108.
[10] TOWATA A, HWANG H J, YASUOKA M, et al. Preparation of polycrystalline YAG/alumina composite fibers and YAG fiber by sol–gel method[J]. Compos Part A Appl Sci Manuf, 2001, 32(8):1127–1131.
[11] DENKI KAGAKU K K. Process for continuous polycrystalline mullite fiber[P]. JP Patent, 260868-A26. 1985–06–03.
[12] KITAOKA S, KAWASHIMA N, KOMATSUBARA Y, et al. Improved filtration performance of continuous alumina-fiber-reinforced mullite composites for hot-gas cleaning[J]. J Am Ceram Soc, 2005, 88(1):45–50.
[13]陆华.氧化铝纤维的制造、性能及应用[J].国外耐火材料, 1997,22(9):19–23.LU Hua. Foreign Refract, 1997, 22(9):19–23.
[14] BHATT R. Modulus, strength and thermal exposure studies of FP-Al2O3/aluminum and FP-Al2O3/magnesium composites[J]. NASA Tech Memo, 1981:1–18.
[15] ALMEIDA R S M, TUSHTEV K, CLAU?B, et al. Tensile and creep performance of a novel mullite fiber at high temperatures[J]. Compos Part A Appl Sci Manuf, 2015, 76:37–43.
[16] ALMEIDA R S M, BERGMüLLER E L, LüHRS H, et al. Thermal exposure effects on the long-term behavior of a mullite fiber at high temperature[J]. J Am Ceram Soc, 2017, 100(9):4101–4109.
[17] BERGER M H, BUNSELL A R. 1.9 oxide fibers[M]//Comprehensive Composite Materials II. Amsterdam:Elsevier, 2018:218–242.
[18] TUSHTEV K, ALMEIDA R S M. Comprehensive composite materials II[M]. Amsterdam:Elsevier, 2018:131–157.
[19] BUNSELL A R. Handbook of tensile properties of textile and technical fibres[M]. Oxford:Woodhead Publishing, 2009.
[20]陈代荣,韩伟健,李思维,等.连续陶瓷纤维的制备、结构、性能和应用:研究现状及发展方向[J].现代技术陶瓷, 2018, 39(3):151–222.CHEN Dairong, HAN Weijian, LI Siwei, et al. Adv Ceram, 2018, 39(3):151–222.
[21] NOURBAKHSH S, LIANG F L, MARGOLIN H. Characterization of a zirconia toughened alumina fibre, PRD-166[J]. J Mater Sci Lett,1989, 8(11):1252–1254.
[22] KOBA K, UTSUNOMIYA T, IWANAGA K, et al. Continuous process for producing long α-alumina fibers[P]. US patent, 4812271. 1989–03–14.
[23]张力.水性溶胶-凝胶法制备Al2O3-SiO2纤维的研究[D].厦门:厦门大学, 2011.ZHANG Li. Study on preparation of Al2O3-SiO2 fiber by aqueous sol-gel method[D]. Xiamen:Xiamen University, 2011.
[24]张继恒.一种SiO2/Al2O3复相陶瓷纤维的制备及力学和热学性能研究[D].哈尔滨:哈尔滨工业大学, 2021.ZHANG Jiheng. Study on the preparation and mechanical and thermal properties of a SiO2/Al2O3 composite ceramic fiber[D]. Harbin:Harbin Institute of Technology, 2021.
[25] EMIG G, WIRTH R, ZIMMERMANN-CHOPIN R. Sol/gel-based precursors for manufacturing refractory oxide fibres[J]. J Mater Sci,1994, 29(17):4559–4566.
[26]姚树玉.莫来石连续纤维制备工艺的研究[D].北京:机械科学研究总院, 2006.YAO Shuyu. Preparing method of continuous mullite fibers[D].Beijing:Institute of Mechanical Sciences, 2006.
[27]王德刚,仲蕾兰,顾利霞.氧化铝纤维的制备及应用[J].化工新型材料, 2002, 30(4):17–19.WANG Degang, ZHONG Leilan, GU Lixia. N Chem Mater, 2002,30(4):17–19.
[28] OKAMURA K. Ceramic fibres from polymer precursors[J].Composites, 1987, 18(2):107–120.
[29] BUNSELL A R. Oxide fibers for high-temperature reinforcement and insulation[J]. JOM, 2005, 57(2):48–51.
[30]黄剑锋.溶胶-凝胶原理与技术[M].北京:化学工业出版社, 2005.
[31] PANDA P K, RAMAKRISHNA S. Electrospinning of alumina nanofibers using different precursors[J]. J Mater Sci, 2007, 42(6):2189–2193.
[32]居学海,范晓薇,马海霞,等.水合铝离子单体和二聚体的DFT研究[J].环境化学, 2007, 26(3):347–351.JU Xuehai, FAN Xiaowei, MA Haixia, et al. Environ Chem, 2007,26(3):347–351.
[33]牛延强.纤维用铝溶胶前驱体的制备及表征[D].济南:山东大学,2020.NIU Yanqiang. Preparation and characterization of aluminum Sol for preparing alumina fibers[D]. Jinan:Shandong University, 2020.
[34] TRIPOL’SKAYA T A, KOLYADINTSEVA L V, MEL’NIK E A, et al.On the stability of Al13 Keggin cation in aqueous hydrogen peroxide solutions[J]. Russ J Inorg Chem, 2017, 62(11):1488–1494.
[35]薛明俊,周世,王淙,等.无机铝溶胶可纺性的研究[J].玻璃与搪瓷, 1994, 22(5):14–21.XUE Mingjun, ZHOU Shi, WANG Cong, et al. Glass Enamel Ophthalmic Opt, 1994, 22(5):14–21.
[36]孟强.氧化铝基陶瓷连续纤维的制备及其性质研究[D].济南:山东大学, 2018.MENG Qiang. Preparation and properties characterization of alumina ceramic continuous fibers[D]. Jinan:Shandong University, 2018.
[37]丁子上,翁文剑.溶胶-凝胶技术制备材料的进展[J].硅酸盐学报,1993, 21(5):443–450.DING Zishang, WENG Wenjian. J Chin Ceram Soc, 1993, 21(5):443–450.
[38]赵婧,李怀祥.溶胶–凝胶法制备无机纳米材料的研究现状[J].微纳电子技术, 2005, 42(11):500–505.ZHAO Jing, LI Huaixiang. Micronanoelectronic Technol, 2005, 42(11):500–505.
[39]任素娥,梁小平,赵素珍,等.溶胶–凝胶法制备氧化铝纤维的研究[J].硅酸盐通报, 2010, 29(4):914–917.REN Sue, LIANG Xiaoping, ZHAO Suzhen, et al. Bull Chin Ceram Soc, 2010, 29(4):914–917.
[40]曹凯,沈湘黔,王涛平,等.溶胶凝胶法制备纳米结构氧化铝陶瓷纤维[J].矿冶工程, 2004, 24(5):76–79.CAO Kai, SHEN Xiangqian, WANG Taoping, et al. Min Metall Eng,2004, 24(5):76–79.
[41]黄前军,陈小君,陈立富.溶胶–凝胶法制备多晶氧化铝纤维的研究[J].厦门大学学报(自然科学版), 2006, 45(3):375–378.HUANG Qianjun, CHEN Xiaojun, CHEN Lifu. J Xiamen Univ Nat Sci, 2006, 45(3):375–378.
[42] CHIOU Y H, TSAI M T, SHIH H C. The preparation of alumina fibre by sol-gel processing[J]. J Mater Sci, 1994, 29(9):2378–2388.
[43] VENKATESH R, RAMANAN S R. Influence of processing variables on the microstructure of sol–gel spun alumina fibres[J]. Mater Lett,2002, 55(3):189–195.
[44]贾玉娜,曹旭,焦秀玲,等.无机酸铝体系氧化铝连续纤维的制备技术研究[J].无机材料学报, 2023, 38(11):1257–1266.JIA Yuna, CAO Xu, JIAO Xiuling, et al. J Inorg Mater, 2023, 38(11):1257–1266.
[45]张鲁,刘陆群,唐赛,等.温度和晶粒尺寸及分布影响下的氧化铝纤维烧结晶粒长大的相场模拟[J].粉末冶金材料科学与工程, 2021,26(4):320–328.ZHANG Lu, LIU Luqun, TANG Sai, et al. Mater Sci Eng Powder Metall, 2021, 26(4):320–328.
[46] LIU Y, ZHANG Z F, HALLORAN J, et al. Yttrium aluminum garnet fibers from metalloorganic precursors[J]. J Am Ceram Soc, 1998, 81(3):629–645.
[47] WU C Z, LIU Q, CHEN R, et al. Mechanism of grain refinement and growth for the continuous alumina fibers by MgO addition[J]. Ceram Int, 2023, 49(5):8565–8575.
[48] MA Y Z, LIU H T, WU C Z, et al. Preparation of high-strength alumina-zirconia fibers by the sol-gel method combined with two-step sintering processes[J]. Ceram Int, 2024, 50(2):4125–4135.
[49] JOHNSON D D. Nextel 312 ceramic fiber from 3M[J]. J Coat Fabr,1981, 10(4):282–296.
[50]贾玉娜,梁可可,焦秀玲,等. Al2O3-SiO2-B2O3连续纤维的制备及力学性能[J].材料导报, 2021, 35(14):14025–14029.JIA Yuna, LIANG Keke, JIAO Xiuling, et al. Mater Rep, 2021, 35(14):14025–14029.
[51] SCHMüCKER M, FLUCHT F, SCHNEIDER H. High temperature behaviour of polycrystalline aluminosilicate fibres with mullite bulk composition. I. Microstructure and strength properties[J]. J Eur Ceram Soc, 1996, 16(2):281–285.
[52]梁可可,贾玉娜,陈代荣,等.含硼氧化铝基陶瓷连续纤维的制备技术[J].宇航材料工艺, 2020, 50(4):39–43.LIANG Keke, JIA Yuna, CHEN Dairong, et al. Aerosp Mater Technol,2020, 50(4):39–43.
[53] PETRY M D, MAH T I. Effect of thermal exposures on the strengths of nextel?550 and 720 filaments[J]. J Am Ceram Soc, 1999, 82(10):2801–2807.
[54]王新刚,杨青青,林根连,等.国产550级连续氧化铝陶瓷纤维的高温拉伸性能研究[J].无机材料学报, 2022, 37(6):629–635.WANG Xingang, YANG Qingqing, LIN Genlian, et al. J Inorg Mater,2022, 37(6):629–635.
[55] LAVASTE V, BERGER M H, BUNSELL A R, et al. Microstructure and mechanical characteristics of alpha-alumina-based fibres[J]. J Mater Sci, 1995, 30(17):4215–4225.
[56] HAY R S, FAIR G E, TIDBALL T. Fiber strength after grain growth in nextel?610 alumina fiber[J]. J Am Ceram Soc, 2015, 98(6):1907–1914.
[57]郭娟妮. α-A12O3连续纤维的制备与表征[D].济南:山东大学,2020.GUO Juanni. Preparation and characterization of α-Al2O3 continuous fiber[D]. Jinan:Shandong University, 2020.
[58] DELéGLISE F, BERGER M H, JEULIN D, et al. Microstructural stability and room temperature mechanical properties of the Nextel 720fibre[J]. J Eur Ceram Soc, 2001, 21(5):569–580.
[59] POULON-QUINTIN A, BERGER M H, BUNSELL A R. Mechanical and microstructural characterisation of Nextel 650 alumina–zirconia fibres[J]. J Eur Ceram Soc, 2004, 24(9):2769–2783.
[60]李萌.溶胶凝胶法制备连续氧化铝纤维的基础研究[D].长沙:国防科学技术大学, 2011.LI Meng. Research of preparation of continuous alumina fibers by sol-gel method[D]. Changsha:National University of Defense Technology, 2011.
[61]孙敬伟,王洪磊,杨蕊,等.热处理环境对Al2O3纤维力学性能及微观结构的影响[J].材料工程, 2023, 51(8):110–119.SUN Jingwei, WANG Honglei, YANG Rui, et al. J Mater Eng, 2023,51(8):110–119.
[62]彭劭恒,姚树伟,王娟,等.加张烧结下连续氧化铝纤维的组织结构演变规律[J].粉末冶金材料科学与工程, 2022, 27(5):542–549.PENG Shaoheng, YAO Shuwei, WANG Juan, et al. Mater Sci Eng Powder Metall, 2022, 27(5):542–549.
[63]王安琪.氧化铝连续纤维的表面改性研究[D].济南:山东大学,2020.WANG Anqi. Surface modification of alumina continuous fiber[D].Jinan:Shandong University, 2020.
[64] SCHMüCKER M, FLUCHT F, MECHNICH P. Degradation of oxide fibers by thermal overload and environmental effects[J]. Mater Sci Eng A, 2012, 557:10–16.
[65]姜如.连续氧化铝纤维增强氧化铝基复合材料的制备与性能研究[D].长沙:国防科技大学, 2019.JIANG Ru. Preparation and performance of continuous alumina fiber reinforced alumina matrix composites[D]. Changsha:National University of Defense Technology, 2019.
[66] HAY R S, ARMANI C J, RUGGLES-WRENN M B, et al. Creep mechanisms and microstructure evolution of Nextel?610 fiber in air and steam[J]. J Eur Ceram Soc, 2014, 34(10):2413–2426.
[67] WILSON D M, LIEDER S L, LUENEBURG D C. Microstructure and high temperature properties of nextel 720 fibers[M]//Proceedings of the19th Annual Conference on Composites, Advanced Ceramics,Materials, and Structures—B:Ceramic Engineering and Science Proceedings, Volume 16, Issue 5. Hoboken, NJ, USA:John Wiley&Sons, Inc., 2008:1005–1014.
[68] ARMANI C J, RUGGLES-WRENN M B, HAY R S, et al. Creep and microstructure of Nextel?720 fiber at elevated temperature in air and in steam[J]. Acta Mater, 2013, 61(16):6114–6124.
[69] BUNSELL A R, BERGER M H. Fine diameter ceramic fibres[J]. J Eur Ceram Soc, 2000, 20(13):2249–2260.
[70]汪家铭,孔亚琴.氧化铝纤维发展现状及应用前景[J].高科技纤维与应用, 2010, 35(4):49–54.WANG Jiaming, KONG Yaqin. Hi Tech Fiber Appl, 2010, 35(4):49–54.
[71]景茂祥,沈湘黔.氧化铝纤维的研究现状与发展趋势[J].矿冶工程,2004, 24(2):69–71.JING Maoxiang, SHEN Xiangqian. Min Metall Eng, 2004, 24(2):69–71.
[72]薛友祥,李福功,唐钰栋,等.高温陶瓷纤维过滤材料[J].现代技术陶瓷, 2020, 41(5):281–293.XUE Youxiang, LI Fugong, TANG Yudong, et al. Adv Ceram, 2020,41(5):281–293.
[73] ROMINE J C. New High-temperature Ceramic Fiber[J]. Ceram. Eng.Sci Proc, 1987, 8(7/8):755–758.
[74]刘威,崔元山,金江.高温除尘用纤维多孔陶瓷材料的制备及性能[J].南京工业大学学报(自然科学版), 2011, 33(4):107–110.LIU Wei, CUI Yuanshan, JIN Jiang. J Nanjing Univ Technol Nat Sci Ed, 2011, 33(4):107–110.
[75]王挺,王三反,陈霞.活性氧化铝除磷吸附作用的研究[J].水处理技术, 2009, 35(3):35–38.WANG Ting, WANG Sanfan, CHEN Xia. Technol Water Treat, 2009,35(3):35–38.
[76]冻瑞岚,彭志航,向阳,等.固含量对浆料浸渍法制备氧化铝陶瓷基复合材料结构与性能的影响[J].材料工程, 2023, 51(8):120–129.DONG Ruilan, PENG Zhihang, XIANG Yang, et al. J Mater Eng, 2023,51(8):120–129.
[77] ZHU C X, CAO F, XIANG Y, et al. Effects of sintering temperature on mechanical properties of alumina fiber reinforced alumina matrix composites[J]. J Sol Gel Sci Technol, 2020, 93(1):185–192.
[78] TANIMOTO Y, NEMOTO K. Development of Al2O3 fiber-reinforced Al2O3-based ceramics[J]. Dent Mater J, 2004, 23(3):297–304.
[79]杨瑞,陈易诚,邓杨芳,等.高温热暴露对Al2O3/Al2O3陶瓷基复合材料性能影响[J].航空材料学报, 2023, 43(2):1–8.YANG Rui, CHEN Yicheng, DENG Yangfang, et al. J Aeronaut Mater,2023, 43(2):1–8.
[80] ZOK F W. Fracture and fatigue of continuous fiber-reinforced metal matrix composites[M]//Comprehensive Composite Materials.Amsterdam:Elsevier, 2000:189–220.
[81]张俊敏,蔡飞燕,靳喜海,等.连续纤维增强陶瓷基复合材料研究与应用进展[J].陶瓷学报, 2023, 44(2):195–207.ZHANG Junmin, CAI Feiyan, JIN Xihai, et al. J Ceram, 2023, 44(2):195–207.
[82] DEVE H E, MCCULLOUGH C. Continuous-fiber reinforced composites:A new generation[J]. JOM, 1995, 47(7):33–37.
[83]戴小亚.连续氧化铝纤维增强铝基复合材料残余应力表征与调控[D].上海:上海交通大学, 2014.DAI Xiaoya. Determination and adjustment of matrix residual stress in continuous alumina fiber-reinforced aluminum composites[D].Shanghai:Shanghai Jiao Tong University, 2014.
[84] 3M Center, Aluminum Conductor Composite Reinforced Technical Notebook. Conductor and Accessory Testing.[EB/OL].[2024–03–01].http://multimedia.3m.com
[85]黄钰刚. ACCR导线在重庆220kV水双南北线路改造中的应用分析[J].电力技术经济, 2009, 21(1):49–53.HUANG Yugang. Electr Power Technol Econ, 2009, 21(1):49–53.
[86]杨韬,马庆强.新一代复合导线:ACCR的特点及其应用[J].电力设备, 2007(12):84–87.YANG Tao, MA Qingqiang. Electr Equip, 2007(12):84–87.
基本信息:
DOI：10.14062/j.issn.0454-5648.20240213
中图分类号:TQ174.758.21
引用信息:
[1]焦秀玲,陈代荣.氧化铝基陶瓷连续纤维研究进展[J].硅酸盐学报,2024,52(08):2738-2754.DOI:10.14062/j.issn.0454-5648.20240213.
基金信息:
山东省自然科学基金(重大基础研究)(ZR2023ZD19)
2024-03-14
2024
2024-06-17
2024
2024-06-20
1
2024-06-17
2024-06-17
2024-06-17