利用微量热分析、X射线衍射、差热分析、扫描电镜和氮气吸附等手段研究了纳米SiO2对硅酸盐水泥水化硬化的影响。结果表明:纳米SiO2掺量为5%(质量分数)时,其高火山灰反应能大量吸收Ca(OH)2,进而促进水泥水化,提高水化开始时的放热速率,并改善水泥浆体的微观结构,使得水泥石更加均一密实。同时,纳米SiO2的掺入使得标准稠度需水量急剧上升,凝结时间缩短,促进水泥石的中后期强度增长。
Abstract：The hydration and hardening of cement-based materials containing nano-silicon dioxide of 5% (in mass) were investigated by microcalorimeter, X-ray diffraction, differential thermal analysis, scanning electron microscope, and nitrogen adsorption. The results show that nano-silicon dioxide can consume large amounts of Ca(OH)2 due to its high pozzolanic activity, so that hydration can be accelerated, the evolution rate of hydration heat in the early period can be increased, the microstructure can be improved and harden cement paste gets more homogeneous and dense. Nano-silicon dioxide can increase water requirement of normal consistency, shorten setting time and enhance com- pressive strength of cement-based materials, especially at middle period and later period.
[1]王少南.纳米技术及其在建材的发展和应用前景[J].化学建材,2001(4):14–17.WANG Shaonan.Chem Constr Mater(in Chinese),2001(4):14–17.
[2]王政.纳米技术与建筑材料工业[J].建材工业信息,2001(5):4–5.WANG Zheng.Build Mater Ind Inform(in Chinese),2001(5):4–5.
[3]关欣,王伟忠.纳米科技及其在建材领域的应用[J].辽宁建材,2002,1:20–21.GUANG Xin,WANG Weizhong.Liaoning Build Mater(in Chinese),2002(1):20–21.
[4]熊国宣,邓敏,宋碧涛,等.纳米材料在混凝土中应用的思考[J].混凝土与水泥制品,2002(5):18–21.XIONG Guoxuan,DENG Min,SONG Bitao,et al.Chin Concr Cem Prod,2002(5):18–21.
[5]陈荣升,叶青.掺纳米SiO2与掺硅粉的水泥硬化浆体的性能比较[J].混凝土,2002,1:7–10.CHEN Rongsheng,YE Qing.Concrete(in Chinese),2002,1:7–10.
[6]唐明,巴恒静,李颖.纳米级SiOx与硅灰对水泥基材料的复合改性效应研究[J].硅酸盐学报,2003,31(5):523–527.TANG Ming,BA Hengjing,LI Ying.J Chin Ceram Soc(in Chinese),2003,31(5):523–527.
[7]王冲,蒲心诚,刘芳,等.纳米颗粒材料在水泥基材料中应用的可行性研究[J].新型建筑材料,2003(2):22–23.WANG Chong,PU Xincheng,LIU Fang,et al.New Build Mater(in Chinese),2003(2):22–23.
[8]王立久,王宝民.纳米SiO2对硅酸盐水泥性能影响实验研究[J].大连理工大学学报,2003,43(5):666–669.WANG Lijiu,WANG Baomin.J Dalian Univ Technol(in Chinese),2003,43(5):666–669.
[9]杨新亚.C80微量热仪在水泥水化研究中的应用[J].水泥,1997,12:9–11.YANG Xinya.Cement(in Chinese),1997,12:9–11.
[10]EVJU C.Initial hydration of cementitious systems using a simple isothermal calorimeter and dynamic correction[J].J Therm Anal Calo-rim,2003,71(3):829–840.
[11]沈威,黄文熙,闵盘荣.水泥工艺学[M].北京:中国建筑工业出版社,1986.141页.SHEN Wei,HUANG Wenxi,MIN Panrong.Cement Technology(in Chinese).Beijing:China Architecture&Building Press,1986.p141.
[12]LANGAN B W,WENG K,WARD M A.Effect of silica fume and fly ash on heat of hydration of Portland cement[J].Cem Concr Res,2002,32:1045–1051.
[13]卢忠远,徐迅.纳米SiO2对硅酸盐水泥水化特性的影响[J].建筑材料学报,2006(10):581–585.LU Zhongyuan,XU Xun.J Build Mater(in Chinese),2006(10):581–585.
基本信息:
中图分类号:TQ172.1
引用信息:
[1]徐迅,卢忠远.纳米二氧化硅对硅酸盐水泥水化硬化的影响[J].硅酸盐学报,2007,No.215(04):478-484.
基金信息:
四川省科学基金(04JY029–060–1)资助项目
2007-04-30
2007-04-30