采用传统的高温熔融法制备了80GeO2–20RO(R=Ca,Sr,Ba)掺铋锗酸盐玻璃。研究了铋掺杂锗酸盐玻璃超宽带近红外发光性质,探讨了铋离子掺杂玻璃超宽带发光机理。结果表明:在808nm激光激发下,铋掺杂锗酸盐玻璃随着碱土金属离子半径增加,中心波长为1300nm的发射强度逐渐降低;在690 nm激光激发下,铋掺杂锗酸盐玻璃的近红外发射覆盖从900 nm到2 000 nm波段但不呈现正态分布,荧光半高宽达428 nm。随着碱土金属离子半径的增加,其近红外发射中心位置逐渐向长波方向移动,推测近红外发光可能源于两种不同形式铋的发光中心。铋掺杂的锗酸盐玻璃具有良好的光学性能,较宽的荧光半高宽,将成为未来超宽带光纤放大器的增益介质。
Abstract：The Bi-doped germanate glass with the molar composition of 80GeO2–20RO(R = Ca,Sr,Ba) was prepared by a conven-tional melting-quenching technique.The broadband infrared luminescence properties of the glasses were investigated.The infrared luminescence intensity decreases with the increase of the radius of alkaline earth ion under 690 nm and 808 nm excitation,respectively.The excitation at 690 nm produces a emission band in the range from 900 to 1 900 nm,and the full width at half a maximum(FWHM) of broad infrared fluorescence reaches up to 428 nm.It is suggested that the infrared emissions could be due to the presence of Bi+ and BiO.The bismuth-doped germanate glass has a superior optical performance with broad FWHM,which could be used as a gain medium of super broadband fiber amplifier in future.
[1]HUANG Lihui,ANIMESH Jha,SHEN Shaoxiong,et al.Broadbandemission in Er3+-Tm3+codoped tellurite fibre[J].Opt Expr,2004,12:2429–2434
[2]ZHOU Dacheng,SONG Zhiguo,CHI Guangwei,et al.NIR broadbandluminescence and energy transfer in Er3+–Tm3+-co-doped telluriteglasses[J].J Alloys Compod,2009,481:881–884.
[3]FUJIMOTO Y,NAKATSUKA M.Infrared luminescence from bis-muth-doped silica glass[J].Jpn J Appl Phys,2001,40:279–281.
[4]BAI Zhenhua,SUN Hongtao,YUJI MIWA,et al.Superbroadband nearinfrared emission from bismuth doped high-silica nanocrystalline zeo-lites[J].237–240.
[5]REN Jinjun,WU Botao,ZHU Congshan,et al.Investigation on theinfrared luminescence from bismuth-doped borate silicate glasses[J].JWuhan Univ Technol Mater,2007,22:817–820.
[6]WANG Xi,ZHOU Shifeng,BAO Jiaxing,et al.,Infrared broadbandemission of bismuth-doped RO-B2O3(R=Ca,Sr,Ba)glasses[J].J Wu-han Univ Technol Mater,2007,22:841–843.
[7]PENG Mingying,WU Botao,DA Ning,et al.Bismuth-activated Lu-minescent Materials for Broadband Optical Amplifier in WDM System[J].J Non-Cryst Solids,2008,354:1221–1225.
[8]FUJIMOTO Y,NAKATSUKA M.Optical amplification in bismuthdoped silica glass[J].Appl Phys Lett,2003,82(19):3325–3326.
[9]ZHOU S F,JIAN N,QIU J R.Multifunctional bismuth-doped nanoporoussilica glass:From blue-green,orange,red,and white light sources toultra-broadband infrared amplifiers[J].Adv Funct Mater,2008,18(9):1407–1413.
[10]SOKOLOV V O,PLOTNICHENKO V G,DIANOV E M.Origin ofbroadband near-infrared luminescence in bismuth-doped glasses[J].Opt Lett,2008,33:1488–1490.
[11]DUFFY A J,INGRAM M.An interpretation of glass chemistry interms of the optical basicity concep[J].J Non-Cryst Solids,1976,21:373–410.
[12]CHI Guangwei,ZHOU Dacheng,SONG Zhiguo,et al,Effect of opticalbasicity on broadband infrared fluorescence in bismuth-doped alkalimetal germanate glasses[J].Opt Mater,2009,31:945–948.
[13]SONG Zhiguo,ZHOU Dacheng,YANG Zhengwen,et al.Correlationbetween optical basicity and properties of broadband infrared fluores-cence of bismuth-doped germanate glasses[J].J Chin Ceram Soc,2010,38:2133–2137.
[14]SHANG Jihua,YANG Zhengwen,LIU Zhiliang,et al.Ultra broadbandnear infrared emission properties of bismuth doped Al2O3-MgO-SiO2glasses[J].J Chin Ceram Soc,2010,38:2129–2132.
[15]FERRARIS M,MILANESE D,CONTARDI C,et al.UV–Vis,FT-IRand EPR investigation on multi-component germano-silicate glassesfor photonics[J].J Non-Cryst Solids,2004,347:246–253.
[16]WANG Jenn-Shing,HON Kuen-Ming,YANG Ko-Ho,et al.Mixedalkali effect on calcium aluminogermanate glasses[J].Ceram Int,1997,23:153–l57.
[17]SALEM-SUQUI S,ALP E E,MINI S M,et al.Phys Rev B,1991,43(7):5511.
[18]SHESTAKOV O,BREIDOHR R,DEMES H,et al.Electronic statesand spectra of BiO[J].J Mol Spectrosc,1998,190(1):28–77.
[19]PENG Mingying,CHEN Danping,QIU Jianrong,et al.Bismuth-dopedzinc aluminosilicate glasses and glass-ceramics with ultra-broadbandinfrared luminescence[J].Opt Mater,2007,29(1):556–561.
[20]SHESTAKOV O,BREIDOHR R,DEMES H,et al.Electronic Statesand Spectra of BiO[J].J Mol Spectrosc,1998,190:28–77.
[21]FINK E H,SETZER K D,RAMSAY D,et al.A new band spectrum ofBiO in the near-infrared region[J].Chem Phys Lett,1991,179:103–108.
[20]BLASSE G,BRIL A.Study of energy transfer from Sb3+,Bi3+,Ce3+toSm3+,Eu3+,Tb3+,Dy3+[J].J Chem Phys,1967,47(6):1920–1926.
[21]SHIN S H,JEON D Y,SUH K S.Charge-transfer nature in lumines-cence of YNbO4:Bi blue phosphor[J].J Appl Phys,2001,90(12):5986.
[22]REN J J,YANG L Y,QIU J R,et al.Effect of various alkaline-earthmetal oxides on the broadband infrared luminescence from bis-muth-doped silicate glasses[J].Solid State Commun,2006,140:38.
基本信息:
中图分类号:TQ171.1
引用信息:
[1]王荣飞,周大成,杨正文,等.铋掺杂锗酸盐玻璃超宽带近红外发光性质及机理[J].硅酸盐学报,2013,41(07):1015-1018.
基金信息:
国家重点基础研究发展计划“973”项目(2011CB211708);; 国家自然科学基金(51002068,51272097,61265004);; 云南省应用基础研究青年基金(2012FD009)资助项目
2013-06-28
2013-06-28
2013-06-28