研究了掺铒钨碲酸盐玻璃的吸收光谱和荧光光谱。应用JuddOfelt理论计算了Er3+的光谱强度参数Ωt(t=2,4,6)、自发辐射跃迁几率、荧光分支比和辐射寿命。从光谱强度参数的计算说明掺铒钨碲酸盐玻璃中Er—O键的共价性强于碲酸盐玻璃中Er—O键的共价性。玻璃的荧光半高宽为52nm,大于Er3+在磷酸盐和硅酸盐玻璃中的荧光半高宽。应用McCumber理论,计算了钨碲酸盐玻璃中Er3+离子在峰值波长1532nm的受激发射截面,为0.91×10-20cm2,大于Er3+在碲酸盐玻璃中的受激发射截面0.75×10-20cm2。由于掺铒钨碲酸盐玻璃的玻璃转变温度高、有较大的声子能量、较宽的荧光半高宽和较大的受激发射截面,是制作高增益的光波导放大器的理想材料。
Abstract:Erbium ion-doped tungstentellurite glass was fabricated and characterized by absorption spectrum and fluorescence spectrum. The intensity parameters Ωt(t=2, 4, 6), spontaneous radiative transition rate, fluorescence branching ratio and radiative lifetime of each energy level of Er3+ were calculated from the absorption spectrum by the JuddOfelt theory. The calculation results of spectroscopic intensity parameters show that the covalency of Er—O bond in Er3+-doped tungstentellurite glass is stronger than that of Er—O bond in tellurite glass. The fluorescence full width at half maximum of 52 nm is larger than that of Er3+ in phosphate and silicate glass. The stimulated emission cross section of Er3+ in tungsten-tellurite glass at 1 532 nm calculated from McCumber theory is 0.91×10-20 cm2, which is larger than that of 0.75×10-20 cm2 for Er3+ in tellurite glass. Er3+-doped tungstentellurite glass has higher glass transition temperature, higher phonon energy, broader fluorescence full width at half maximum and larger stimulated emission cross section, so it is an ideal host material for the fabrication of high gain Er3+-doped waveguide amplifier.
[1] YAMADAM,MORIA,KOBAYASHIK.Gain flattenedtellurite basedEDFAwithaflatamplificationbandwidthof76nm[J].PhotonicsTechnolLett,1998,10:1244—1246.
[2] DINGY ,JIANGSB ,HWANGBC .Spectralpropertiesofer bium dopedleadhalotelluriteglassesfor1.5μmbroadbandampli fication[J].OptMater,2000,15(2):123—130.
[3] MORIA ,KOBAYASHIK ,YAMADAM ,etal.Lownoisebroadbandtellurite basedEr3+ dopedfibreamplifiers[J ].ElectronLett,1998,34:887—888.
[4] CONTIGN ,TIKHOMIROVVK ,CHENB ,etal.Ion ex changedplanarwaveguidesindifferentEr3+ dopedtelluriteglass es[J].SPIE ,2003,4990:97—102.
[5] DINGY ,JINAGS ,LUOT ,etal.Opticalwaveguidespre paredinEr3+ dopedtelluriteglassbyAg+Na+ ionexchange[J].SPIE ,2001,4282:23—30.
[6] KOSUGET ,BENINOY ,DIMITROVV ,etal.Thermalsta bilityandheatcapacitychangesattheglasstransitioninK2OWO3TeO2 glasses[J].JNonCrystSolids,1998,242(2/3):154—164.
[7] JUDDBR .Opticalabsorptionintensitiesofrare earthions[J].PhysRev,1962,127:750—761.
[8] OFELTGS .Intensitiesofcrystalspectraofrare earthions[J].JChemPhys,1962,37:511—520.
[9] LINH ,PUNEYB ,MANSQ ,Opticaltransitionsandfre quencyupconversionofEr3+ ionsinNa2OCa3Al2Ge3O12 glasses[J].JOptSocAmB ,2001,18:602—609.
[10] MCCUMBERDE .Theoryofphonon terminatedopticalmasters[J].PhysRevA ,1964,134:299—306.
[11] MINISCALCOWJ ,QIUMBYRS .GeneralprocedurefortheanalysisofEr3+ crosssections[J].OptLett,1991,16:258—260.
[12] SANDOEJN ,SARKIESPH ,PARKES .VariationofEr3+crosssectionforstimulatedemissionwithglasscomposition[J].JPhysD :AppPhys,1972,5:1788—1799.
基本信息:
DOI:
中图分类号:TQ171
引用信息:
[1]赵士龙,陈宝玉,胡丽丽.掺铒钨碲酸盐玻璃光谱性质的研究[J].硅酸盐学报,2004(11):1430-1432+1436.
基金信息:
上海光科技(002261002)资助项目。